对工业实验生产的X90级第三代管线钢的力学性能与组织特征进行了研究.结果表明,工业试生产的18.4 mm厚X90管线钢板微观组织是以准多边形铁素体、板条贝氏体及其中的M/A(马氏体/奥氏体)为主的多相组织.钢板的屈服强度达到615-660 MPa,抗拉强度达到720 MPa以上,屈强比不大于0.9,-30℃冲击功达到200 J,-15℃落锤撕裂实验(DWTT)韧性剪切面积大于80%.实验钢中“软相”(准多边形铁素体)与“硬相”(板条贝氏体)的比例约为3:2,板条贝氏体组织位错密度高,而准多边形铁索体的位错密度较低.EBSD结果表明,工业实验钢“硬相”组织中的板条之间呈现切变转变特征,已达到软硬相多相组织的调控效果.
参考文献
[1] | Ishikawa N,Okastu M,Endo S,Kondo J.6th Int Pipeline Conf,Calgary:AMSE,2006:1 |
[2] | Shang C J,Wang X M,Liu Q Y,Fu J Y.Int Seminar on Welding of Pipeline Steel,Arasa:December,2011 |
[3] | Ishikawa N,Endo S,Kondo J.JFE Technol Report,2006; 7:20 |
[4] | Okatsu M,Shikanai N,Kondo J.JFE Technol Report,2008; 12:8 |
[5] | Zheng L,Fu J Y.Iron Steel,2006; 41:1(郑磊,付俊岩.钢铁,2006; 41:1) |
[6] | Suzuki N,Masamura K.Pipeline Technology Conference,Ostend:Laboratorium Soete and TI-KVIV,2009:1 |
[7] | Zheng L,Gao S.In the Development of High Performance Pipeline Steel in China.Beijing:Petroleum Storage &Transformation Committee Of China Petroleum Society,2008:95(郑磊,高珊.北京管线钢国际研讨会论文集.北京:中国石油学会石油储运委员会,2008:95) |
[8] | Li H L,Jj L K.World Iron Steel,2009; (1):56(李鹤林,吉玲康.世界钢铁,2009; (1):56) |
[9] | Sun X J,Li Z D,Yong Q L,Yang Z G,Weng Y Q.Sci China Technol Sci,2012; 55:1797 |
[10] | Nie W J,Shang C J,Guan H L,Zhang X B,Chen S H.Acta Metall Sin,2012; 48:298(聂文金,尚成嘉,关海龙,张晓兵,陈少慧.金属学报,2012; 48:298) |
[11] | Nie W J,Shang C J,You Y,Zhang X B,Subramanian S V.Acta Metall Sin,2012; 48:797(聂文金,尚成嘉,由洋,张晓兵,Subramanian S V.金属学报,2012; 48:797) |
[12] | Nie W J,Wang X M,Wu S J,Guan H L,Shang C J.Sci China Technol Sci,2012; 55:1791 |
[13] | Li X C,Xia D X,Wang X L,Wang X M,Shang C J.Sci China Technol Sci,2012; 55:1 |
[14] | Shang C J.Echnology Forum on High Grade Pipeline Steels for Oil & Gas Industry-New Challenges for Steels from Strategic Demand of Exploration and Transportation of Oil & Gas,Beijing:Chinese Society for Metals (CSM),2011:55(尚成嘉.石油天然气用高性能钢技术论坛-油气开采、储运的战略需求对钢铁材料的新挑战,北京:中国金属学会,2011:55) |
[15] | Bhadeshia H D K H.Bainite in Steels.2nd Ed.,London:The Cambridge University Press,2001:142 |
[16] | Miao C L,Shang C J,Zhang G D,Subramanian S V.Mater Sci Eng,2010; A527:4985 |
[17] | Miao C L,Shang C J,Zurob H S,Zhang G D,Subramanian S V.Metall Mater Trans,2012; 43A:665 |
[18] | He X L,Shang C J.High Performance Low Carbon Bainte Steel.Beijing:Metallugical Industry Press,2008:148(贺信莱,尚成嘉.高性能低碳贝氏体钢.北京:冶金工业出版社,2008:148) |
[19] | Diazfuentes M,Izamendia A,Gutierrez I.Metall Mater Trans,2003; 34A:2005 |
[20] | Miao C L,Shang C J,Wang X M,Zhang L F,Subramanian S V.Acta Metall Sin,2010; 46:545(缪成亮,尚成嘉,王学敏,张龙飞,Subramanian S V.金属学报,2010; 46:545) |
[21] | You Y,Shang C J,Chen L,Subramanian S V.Mater Sci Eng,2012; A546:111 |
[22] | Miyamoto N,Takayama G,Furuhara T.Scr Mater,2009;60:1113 |
[23] | Kitahara H,Ueji R,Tsuji N,Minamino Y.Acta Mater,2006; 54:1279 |
[24] | Miao C L,Shang C J,Subramanian S V.J Univ Sci Technol Beijing,2012; 34:289(缪成亮,尚成嘉,Subramanian S V.北京科技大学学报,2012;34:289) |
[25] | Cui G B,Guo H,Yang S W,He x L.Acta Metall Sin,2009; 45:680(崔桂彬,郭晖,杨善武,贺信莱.金属学报,2009; 45:680) |
[26] | Guo Z,Lee C S,Morris J W.Acta Mater,2004; 52:5511 |
[27] | Morris J W,Lee C S,Guo Z.ISIJ Int,2003; 43:410 |
[28] | Kumar A,Singh S B,Ray R K.Mater Sci Eng,2008;A474:270 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%