采用直接水冷连续铸造法制备了3003/4004铝合金复层圆铸坯,使用OM,SEM和EPAM对复层铸锭界面凝固组织及元素分布进行了系统的检测,并对3003/4004铝合金复层铸坯进行拉伸实验,分析其界面结合强度.OM结果表明,直接水冷连续铸造法所制备的3003/4004铝合金复层圆铸坯界面清晰,无气孔、夹杂等缺陷,整个铸锭断面大部分为等轴晶组织.利用EPAM对结合界面进行线扫描分析,结果表明,3003和4004铝合金溶质元素间发生了相互扩散,形成厚度约为30 μm的扩散层.复层铸坯拉伸实验结果表明,3个拉伸试样都在强度较低的3003铝合金一侧断裂,试样抗拉强度为107.7 MPa,说明复层铸坯界面结合强度高于3003铝合金抗拉强度,界面结合牢固.
参考文献
| [1] | Sun J B,Song X Y,Wong T M,Yu Y S,Sun M,Cao Z Q,Li T J.Mater Lett,2012; 67:21 |
| [2] | Peng X K,Heness G,Yeung W Y.J Mater Sci,1999; 34:277 |
| [3] | Manesh H D,Taheri A K.Mech Mater,2005; 37:531 |
| [4] | Eizadjou M,Manesh H D,Janghorban K.Mater Des,2008; 29:909 |
| [5] | Wang T M,Li J,Du Y Y,Yang Z M,Sun J B,Cai H W,Xu J J,Li T J.Mater Res Inn,2010; 14:271 |
| [6] | Xiong B W,Cai C C,Wan H,Lu B P.Mater Des,2011;32:2978 |
| [7] | Ramazan K,Mustafa A.J Mater Proc Technol,2004; 152:91 |
| [8] | Akbari-Mousavi S A A,Barrett L,Al-Hassani S T S.J Mater Proc Technol,2008; 202:224 |
| [9] | Ahmet D,Behcet G,Fehim F.Mater Des,2005; 26:497 |
| [10] | Liu D Y,Liu S C,Chen R S,Wang X F.Trans Mater Heat Treat,2007; 28:110(刘德义,刘世程,陈汝淑,王晓峰.材料热处理学报,2007; 28:110) |
| [11] | Qu S J,Geng L,Cao G J,Lei T Q.Acta Mater Compos Sin,2003; 20(3):69(曲寿江,耿林,曹国剑,雷廷权.复合材料学报,2003; 20(3):69) |
| [12] | Takeuchi E,Zene M.Iron Steel,1997; 24:257 |
| [13] | Wang Z T.Light Alloy Fabr Technol,2007; 35:1(王祝堂.轻合金加工技术,2007; 35:1) |
| [14] | Zhang W W,Zou G F,Deng C N.Acta Metall Sin,1998;34:609(张卫文,邹敢峰,邓长宁.金属学报,1998; 34:609) |
| [15] | Zhang W W,RohatgiP K,Shao M,Li Y Y.Mater Sci Eng,2009; A505:120 |
| [16] | Wu C J,Yu Z M,Xie J X,Wu Y.Foundry,2004; 53:432(吴春京,于治民,谢建新,吴渊.铸造,2004; 53:432) |
| [17] | Xie J X,Wu C J,Zhou C.Chin Pat,01109076.6,2002(谢建新,吴春京,周成.中国专利,01109076.6,2002) |
| [18] | Xue Z Y,Qin Y Q,Wu C J.JUniv Sci Technol Beijing,2005; 27:706(薛志勇,秦延庆,吴春京.北京科技大学学报,2005; 27:706) |
| [19] | Xue Z Y,Wu C J,Xie J X.Spec Cast Nonferrous Alloys,2006; 26:101(薛志勇,吴春京,谢建新.特种铸造及有色合金,2006; 26:101) |
| [20] | Xu F,Zhang W W,Luo Z Q,Kang Z X.Spec Cast Nonferrous Alloys,2007; 27:624(许峰,张卫文,罗宗强,康志新.特种铸造及有色合金,2007;27:624) |
| [21] | Song X Y,Sun J B,Zhong D S,Yu Y S,Wang T M,Cao Z Q,Li T J.Mater Res Inn,2012; 16:51 |
| [22] | Cao Z Q,Liu B,Sun J B,Song X Y,Sun M,Wang T M,Li T J.J Wuhan Univ Sci Technol,2012; 35:19(曹志强,刘彬,孙建波,宋晓阳,孙敏,王同敏,李廷举.武汉科技大学学报,2012; 35:19) |
| [23] | Wu C H.Master Thesis,Dalian University of Technology,2005(吴彩虹.大连理工大学硕士学位论文,2005) |
| [24] | Li Y T.Master Thesis,Dalian University of Technology,2003(李玉婷.大连理工大学硕士学位论文,2003) |
| [25] | Zhang X Z,NaX Z,Wang Z Y,Liu A Q,Gan Y.Acta Metall Sin,2004; 40:281(张兴中,那贤昭,王忠英,刘爱强,干勇.金属学报,2004; 40:281) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%