通过OM显微组织观察、XRD和室温单轴拉伸实验对不同C含量(0.1％和0.2％,质量分数)的冷轧C-Mn-Al-Si系低合金TRIP钢不同热处理工艺下所得组织及其力学行为进行了研究.结果表明:在相同的贝氏体区等温时间下,与低C含量的钢相比,C含量较高的钢获得了相对较少的贝氏体和较多的马氏体,并且表现出较高的强度和延伸率；钢组织中较高的C含量和残余奥氏体含量使其在拥有高强度的同时具有更高的延伸率.拉伸变形过程中应变诱导马氏体相的生成速率与增量应变硬化指数n曲线具有很好的对应关系,体现了TRIP效应对其变形过程中加工硬化能力的决定作用.
参考文献
| [1] | De Cooman B C.Curr Opin Solid State Mater Sci,2004;8:285 |
| [2] | Jacques P J,Girault E,Harlet Ph,Delannay F.ISIJ Int,2001; 41:1061 |
| [3] | Wang X D,Wang L,Rong Y H.Heat Treat,2008; 23:8(王晓东,王利,戎咏华.热处理,2008; 23:8) |
| [4] | Wei X C,Li L,Fu R Y.J Iron Steel Res,2001; 13:71(韦习成,李麟,符仁钰.钢铁研究学报,2001:13:71) |
| [5] | Jacques P J,Girault E,Mertens A,Verlinden B,Humbeeck J,Delannay F.ISIJ Int,2001; 41:1068 |
| [6] | De Meyer M,Vanderschueren D,De Cooman B C.ISIJ Int,1999; 39:813 |
| [7] | Mahieu J,Maki J,De Cooman B C,Claessens S.Metall Mater Trans,2002; 33A:2573 |
| [8] | Yin Y Y,Yang W Y,Li L F,Sun Z Q,Wang X T.Acta Metall Sin,2008; 44:1292(尹云洋,杨王玥,李龙飞,孙祖庆,王西涛.金属学报,2008; 44:1292) |
| [9] | Xu K,Liu G Q.Trans Mater Heat Treat,2009; 30:68(徐锟,刘国权.材料热处理学报,2009; 30:68) |
| [10] | Jing C N,Liu Z X,Wang Z C,Wang M G,Kim S J.J Univ Sci Technol Beijing,2008; 30:610(景财年,刘在学,王作成,王明钢,金成俊.北京科技大学学报,2008; 30:610) |
| [11] | Li Z,Wu D,Wang J F.J Northeast Univ (Nat Sci),2005;26:452(李壮,吴迪,王佳夫.东北大学学报(自然科学版),2005; 26:452) |
| [12] | Jacques P J.Curr Opin Solid State Mater Sci,2004; 8:259 |
| [13] | Miller R L.Trans ASM,1964; 57:892 |
| [14] | Emadoddin E,Akbarzadeh A,Daneshi G H.Mater Charact,2006; 57:408 |
| [15] | Sakuma Y,Matsumura O,Akisue O.ISIJ Int,1991; 31:1348 |
| [16] | Chiang J,Lawrence B,Boyd J D,Pilkey A K.Mater Sci Eng,2011; A528:4516 |
| [17] | Moat R J,Zhang S Y,Kelleher J,Mark A F,Mori T,Withers P J.Acta Mater,2012; 60:6931 |
| [18] | Haidemenopoulos G N,Vasilakos A N.Steel Res,1996; 67:513 |
| [19] | Bourell D L,Rizk A.Acta Metall,1983; 31:609 |
| [20] | Davies R G.Metall Trans,1979; 10A:1549 |
| [21] | Sachdev A K.Acta Metall,1983; 31:2037 |
| [22] | Jacques P J,Furnemont Q,Mertens A,Delannay F.Philos Mag,2001; 81A:1789 |
| [23] | Tsukatani I,Hashimoto S I,Inoue T.ISIJ Int,1991; 31:992 |
| [24] | Olson G B,Cohen M.Metall Trans,1975; 6A:791 |
| [25] | Samek L,De Moor E,Penning J,De Cooman B C.Metall Trans,2006; 36A:109 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%