研究了铸态Ag-In-Cd合金在300-400℃及12-24MPa压应力范围内的压缩蠕变行为,根据实验结果计算了表观应力指数n和表观激活能Qa,探讨了合金的压缩蠕变机制.结果表明,随温度和应力的升高,合金的稳态蠕变速率增加,稳态蠕变速率与应力之间呈指数关系.温度为300,350和400℃时,合金的n分别为2.90,4.09和5.77;压应力为12,18和24 MPa时,合金的Qa值分别为68.1,103.7和131.6 kJ/mol.位错运动形成大量层错是Ag-In-Cd合金在温度为300-400℃,压应力为12-24 MPa下的压缩蠕变控制机制.
参考文献
[1] | Bourgoin J,Couvreur F,Gosset D,Defoort F,Monchanin M,Thibault X.J Nucl Mater,1999; 275:296 |
[2] | Xue S J,Chen Y,Qiu S Y.Nucl Power Eng,2004; 25:522(薛淑娟,陈勇,邱绍宇.核动力工程,2004; 25:522) |
[3] | Devan K,Riyas A,Alagan M,Mohanakrishnan P.Ann Nucl Energy,2008; 35:1484 |
[4] | Sepold L,Lind T,Pintér C A,Stegmaier U,Steinbriick M,Stuckert J.Ann Nucl Energy,2009; 36:1349 |
[5] | Amir H F,Saeed S.Prog Nucl Energy,2009; 51:184 |
[6] | Mousavi S S A,Aghanajafi C,Sadoughi S,Sharifloo N.Ann Nucl Energy,2010; 37:1659 |
[7] | Dubourg R,Austregesilo H,Bals C,Barrachin M.Prog Nucl Energy,2010; 52:97 |
[8] | Tian S G,Zhang J H,Jin T,Yang H C,Xu Y B,Hu Z Q.Acta Metall Sin,1999; 35:392(田素贵,张静华,金涛,杨洪才,徐永波,胡壮麒.金属学报,1999; 35:392) |
[9] | Sha Y H,Zuo L,Zhang J H,Xu Y B,Hu Z Q.Acta Metall Sin,2011; 37:1142(沙玉辉,左良,张静华,徐永波,胡壮麒.金属学报,2011:37:1142) |
[10] | Wei S H,Chen Y G,Tang Y B.Liu H M,Xiao S F,Niu G,Zhang X P,Zhao Y H.Mater Sci Eng,2008; A492:20 |
[11] | Huang C,Yu X H,Yamabe M Y,Nakazawa S,Harada H.Mater Lett,2003; 57:3371 |
[12] | Wei S H,Chen Y G,Tang Y B,Liu M,Xiao S F,Zhang X P,Zhao Y H.Trans Nonferrous Met Soc,2008; 18:214 |
[13] | Wei X W,Shen B L.Mater Sci Technol,2004; 12:642(魏晓伟,沈保罗.材料科学与工艺,2004; 12:642) |
[14] | Ren W L,Guo J T,Zhou J Y.Acta Metall Sin,2002; 38:908(任维丽,郭建亭,周继扬.金属学报,2002:38:908) |
[15] | Fu X W,Yang W L,Zhang L Q.Acta Metall Sin,2002;38:731(傅晓伟,杨王朗,张来启.金属学报,2002; 38:731) |
[16] | Pekguleryuz M O,Kaya A A.Adv Eng Mater,2003; 5:866 |
[17] | Zeng M,Xu D F,Shen B L.Mater Heat Treat,2008; 37:17(曾明,徐道芬,沈保罗.材料热处理技术,2008; 37:17) |
[18] | Liu X Y,Pan Q L,Lu Z L,Cao S F,He Y B,Li W B.Acta Metall Sin,2011; 47:53(刘晓艳,潘清林,陆智伦,曹素芳,何运斌,李文斌.金属学报,2011;47:53) |
[19] | Xu C M.Guo J T.Acta Metall Sin,2003; 39:809(徐春梅,郭建亭.金属学报,2003; 39:809) |
[20] | Weetman J.J Appl Phys,1957; 28:362 |
[21] | Coble R L.J Appl Phys,1963; 34:1679 |
[22] | Sherby O D,Burke P M.Prog Mater Sci,1968; 13:325 |
[23] | Cannon W R,Sherby O D.Metall Trans,1970; 1:1030 |
[24] | Luo A A.Int Mater Rev,2004; 49:13 |
[25] | Yan J L,Sun Y S,Xue F.Acta Metall Sin,2008; 44:1354(晏井利,孙扬善,薛烽.金属学报,2008; 44:1354) |
[26] | Wei S H,Chen Y G,Tang Y B,Zhang X P,Liu M,Xiao S F,Zhao Y H.Mater Sci Eng,2009; A508:59 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%