研究了二元Cu-Cr合金Cu-0.5Cr,Cu-7.0Cr和Cu-15.0Cr(原子分数,％)在700和800℃空气中的高温氧化行为.合金的氧化动力学基本遵循抛物线规律,其中Cu-0.5Cr合金的氧化近似于纯Cu的氧化行为,氧化产物主要为Cu的氧化物,Cr2O3颗粒弥散分布于氧化膜内层靠近膜/基体界面;Cu-7.0Cr和Cu-15.0Cr氧化后外层形成CuO和Cu2O,内层为Cr2O3和Cu2O·Cr2O3混合氧化物,并含有部分未氧化的Cr颗粒.合金的氧化速率随Cr含量的增加而降低,并且β相尺寸减小也利于提高Cu-Cr合金的抗氧化能力.合金氧化膜结构和生长规律与合金的原始显微组织和β相分布状态有关.
参考文献
| [1] | Dou Z H,Zhang Y A,He J C,Jiang X L.Mater Rev,2005; 19(10):63(豆志河,张延安,赫冀成,蒋孝丽.材料导报,2005:19(10):63) |
| [2] | Wang S Y,Gesmundo F,Wu W T,Niu Y.ScrMater,2006; 54:1563 |
| [3] | Zhang K,Niu Y,Li Y S,Wu W T.Rare Met Mater Eng,2004; 33:1287(张轲,牛焱,李远士,吴维弢.稀有金属材料与工程,2004; 33:1287) |
| [4] | Wang S Y,Pan T J,Wang S,Niu Y.High Temp Mater Proc,2006;25:225 |
| [5] | Fu G Y,Niu Y,Wu W T.Acta Metall Sin,1998; 34:159(傅广艳,牛焱,吴维弢.金属学报,1998; 34:159) |
| [6] | Fu G Y,Niu Y,Wu W T.Chin JNonferrous Met,2000; 10:32(付广艳,牛焱,吴维弢.中国有色金属学报,2000; 10:32) |
| [7] | Fu G Y,Niu Y,Wu W T,Guan H R.Trans Nonferrous Met Soc Chin,2001; 11:333 |
| [8] | Gesmundo F,Viani F,Niu Y,Douglass D L.Oxid Met,1993; 40:373 |
| [9] | Gesmundo F,Niu Y,Viani F.Oxid Met,1995; 43:379 |
| [10] | Niu Y,Gesmundo F,Viani F,Rizzo F,Monteiro M J.Corros Sci,1996; 38:193 |
| [11] | Niu Y,Gesmundo F,Viani F,Douglass D L.OxidMet,1997; 48:357 |
| [12] | Huang Z P,Peng X,Wang F H.Acta Metall Sin,2006; 42:290(黄忠平,彭晓,王福会.金属学报,2006; 42:290) |
| [13] | Niu Y,Wang S Y,Gesmundo F.Oxid Met,2006; 65:285 |
| [14] | Ma J,He Y D,Gao W,Wang J,Sun B D.Mater Sci Eng,2008;A488:311 |
| [15] | Mu(N)oz-Morris M A,Valdés León K,Caballero F G,Morris D G.ScrMater,2012; 67:806 |
| [16] | Xu C Z,Wang Q J,Zheng M S,Zhu J W,Li J D,Huang M Q,Jia Q M,Du Z Z.Mater Sci Eng,2007; A459:303 |
| [17] | Gu X L,Ye Y F,Tian Q H,Cheng Y F,Shi L D.Mater Mech Eng,2006; 30(3):51(顾小兰,叶以富,田秋红,程勇锋,施利旦.机械工程材料,2006; 30(3):51) |
| [18] | Li T F.High-temperature Oxidation and Hot Corrosion of Metals.Beijing:Chemical Industry Press,2003:178(李铁藩.金属高温氧化和热腐蚀.北京:化学工业出版社,2003:178) |
| [19] | Fu G Y,Su Y,Liu Q,Cai L,Zhang H L.Rare Met Mater Eng,2007; 36 (suppl 3):259(付广艳,苏勇,刘群,蔡璐,张宏亮.稀有金属材料与工程,2007; 36(增刊3):259) |
| [20] | Liang Y J,Che Y C.Handbook of Thermodynamic Data of Inorganic Compounds.Shenyang:Northestem University Press,1993:1(梁英教,车荫昌.无机物热力学数据手册.沈阳:东北大学出版社,1993:1) |
| [21] | Fu G Y,Niu Y,Wu W T.Acta Metall Sin,2003; 39:297(付广艳,牛焱,吴维弢.金属学报,2003; 39:297) |
| [22] | Zhang X J,Gao C X,Sun L,Wang S J.Rare Met Mater Eng,2008; 37:1078(张学军,高春香,孙伶,王淑菊.稀有金属材料与工程,2008;37:1078) |
| [23] | Cao Z Q,Niu Y,Wu W T.Acta Metall Sin,2000; 36:647(曹中秋,牛焱,吴维弢.金属学报,2000; 36:647) |
| [24] | Fu G Y,Niu Y,Wu W T.Acta Metall Sin,2001; 37:1079(付广艳,牛焱,吴维弢.金属学报,2001; 37:1079) |
| [25] | Cao Z Q,Niu Y,Wu W T.Rare Met Mater Eng,2003; 32:1016(曹中秋,牛焱,吴维弢.稀有金属材料与工程,2003:32:1016 |
| [26] | Myung J S,Lim H J,Kang S G.Oxid Met,1999; 51:79 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%