采用表面机械磨擦处理(SMGT)在Fe-20Mn-3Al-3 Si钢的表面制备梯度相变强化层,并研究了该强化层的微观组织和硬度.结果表明,在SMGT过程中,Fe-20Mn-3Al-3Si钢的表层非常容易发生γ→ε→α马氏体相变.SMGT相变受晶粒取向和外力的共同影响:在小载荷SMGT下,晶粒的{111}或者{110}晶面越靠近试样的表面越容易形成片条状组织;在大载荷SMGT下,表层晶粒严重细化,次表层中片条组织最多,然后片条组织数量逐渐减少.室温车削形成的强化层厚度大于400 μm,硬度在表面最高(450 HV),然后随深度增加而逐渐下降至基体硬度(约220HV).另外,SMGT强化层的热稳定性高,经400℃,lh退火后其微观组织和硬度基本不变.
参考文献
| [1] | Grassel O,Kruger L,Frommeyer G,Meyer L W.Int J Plast,2000;16:1391 |
| [2] | Frommeyer G,Brüx U,Neumann P.ISIJInt,2003; 3:438 |
| [3] | Mi Z L,Tang D,Yan L,Guo J.JMater Sci Technol,2005; 4:451 |
| [4] | Ding H,Ting Z Y,Li W,Wang M,Song D.J Iron Steel Res Int,2006; 6:66 |
| [5] | Long C X.Master Thesis,Hunan University,Changsha,2012 (龙彩霞.湖南大学硕士学位论文,长沙,2012) |
| [6] | Xie P,Wu C L,Ai B B,Chen W L,Chen Y,Chen Y.J Chin Electr Microsc Soc,2013; 32:211 (谢盼,伍翠兰,艾倍倍,陈汪林,陈燕,陈亚.电子显微学报,2013; 32:211) |
| [7] | Wu C L,Ai B B,Xie P,Chen W L,Li J M.JHunan Univ (Nat Sci),2013; 40(6):80 (伍翠兰,艾倍倍,谢盼,陈汪林,李久茂.湖南大学学报(自然科学版),2013;40(6):80) |
| [8] | Long C X,Wu C L,Wang S B.JHunan Univ (Nat Sci),2012; 39 (7):70 (龙彩霞,伍翠兰,王双宝.湖南大学学报(自然科学版),2012;39(7):70) |
| [9] | Ding H,Ding H,Song D,Tang Z Y,Yang P.Mater Sci Eng,2011;A528:868 |
| [10] | Ding H,Ding H,Tang Z Y,Song D,Yang P.Chin J Mater Res,2009; 4:375 (丁昊,丁桦,唐正友,宋丹,杨平.材料研究学报,2009;4:375) |
| [11] | Zhang S J,Ding H,Ding H,Zeng J M,Tang Z Y.J Mater Metall,2009; 3:198 (张淑娟,丁桦,丁昊,曾建敏,唐正友.材料与冶金学报,2009;3:198) |
| [12] | Wang Z B,Yong X P,Tao N R,Li S,Liu G,Lv J,Lu K.Acta MetallSin,2001; 37:1251 (王镇波,雍新平,陶乃镕,李曙,刘刚,吕坚,卢柯.金属学报,2001;37:1251) |
| [13] | Tao N R,Wang Z B,Tong W P,Sui M L,Lu J,Lu K.Acta Mater,2002; 50:4603 |
| [14] | Chen X H,Lu J,Lu L,Lu K.ScrMater,2005; 52:1039 |
| [15] | Liu G,Wang S C,Lou X F,Lu J,Lu K.ScrMater,2001; 44:1791 |
| [16] | Li W L,Tao N R,Lu K.ScrMater,2008; 59:546 |
| [17] | Fang T H,Li W L,Tao N R,Lu K.Science,2011; 331:1587 |
| [18] | Zheng Z J,Gao Y.J Mater Eng,2008; (10):137(郑志军,高岩.材料工程,2008; (10):137) |
| [19] | Amar K D,David C M,Martin C M,John G S,David K M.Scr Mater,2004; 50:1445 |
| [20] | Cong Q Z.Two-dimensional Polycrystalline X-ray Diffraction.Beijing:Science Press,1997:37 (从秋滋.多晶二维X射线衍射.北京:科学出版社,1997:37) |
| [21] | Yong X P,Liu G,Lv J,Lu K.Acta Metall Sin,2002; 38:157 (雍兴平,刘刚,吕坚,卢柯.金属学报,2002; 38:157) |
| [22] | Kleber X,PirfoBarroso S.Mater Sci Eng,2010; A527:6046 |
| [23] | Yu Q M,Hu B F,Chen H M.J Beijing Univ Sci Technol,2002;26:614 (余泉茂,胡本芙,陈焕铭.北京科技大学学报,2002; 26:614) |
| [24] | Wang B Q,Gu N J,Guo S Z,Ma X L.Acta Metall Sin,2002; 38:474 (王宝奇,谷南驹,郭素珍,马晓莉.金属学报,2002; 38:474) |
| [25] | Wang H T,Tao N R,Lu K.Acta Mater,2012; 60:4027 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%