通过强制冷却的搅拌摩擦加工(FSP)技术在Cu-Al合金中得到了超细晶和纳米结构的微观组织,利用电子背散射衍射、透射电子显微镜等技术研究了层错能对FSP Cu-Al合金微观组织和力学性能的影响.结果表明,FSP Cu-Al合金为均匀、等轴的再结晶组织,随着层错能的减小,晶粒尺寸不断降低,而且在低层错能的FSP Cu-Al合金中,超细晶粒内部生成了丰富的纳米孪晶片层组织,进一步细化了微观组织.由于微观组织的逐步细化,FSP Cu-Al合金的强度随层错能的降低逐步提高,而均匀延伸率呈现出先增加后减小的趋势.
参考文献
[1] | Valiev R.NatMater,2004; 3:511 |
[2] | Zhu Y T,Liao X Z.Nat Mater,2004; 3:351 |
[3] | Tao N R,Lu K.J Mater Sci Technol,2007; 23:771 |
[4] | Mughrabi H,Hoppel H W.Int J Fatigue,2010; 32:1413 |
[5] | Goto M,Han S Z,Euh K,Kang J H,Kim S S.Acta Mater,2010;58:6249 |
[6] | An X H.PhD Dissertation,Institute of Metal Research,Chinese Academy of Sciences,2012(安祥海.中国科学院金属研究所博士学位论文,沈阳,2012) |
[7] | Mishra R S,Mahoney M W,McFadden S X,Mara N A,Mukherjee AK.ScrMater,1999; 42:163 |
[8] | Mishra R S,Ma Z Y.Mater Sci Eng,2005; R50:1 |
[9] | Ma Z Y.Metall Mater Trans,2008; 39A:642 |
[10] | Xue P,Xiao B L,Ma Z Y.Mater Sci Eng,2012; A532:106 |
[11] | Su J Q,Nelson T W,Sterling C J.Scr Mater,2005; 52:135 |
[12] | Xue P,Xiao B L,Ma Z Y.ScrMater,2013; 68:751 |
[13] | Chang C I,Du X H,Huang J C.Scr Mater,2007; 57:209 |
[14] | Xue P,Xiao B L,Wang W G,Zhang Q,Wang D,Wang Q Z,Ma Z Y.Mater Sci Eng,2013; A575:30 |
[15] | Xue P,Xiao B L,Ma Z Y.JMater Sci Technol,2013; 29:1111 |
[16] | An X H,Lin Q Y,Wu S D,Zhang Z F,Figueiredo R B,Gao N,Langdon T G.Scr Mater,2011; 64:954 |
[17] | Qu S,An X H,Yang H J,Huang C X,Yang G,Zang Q S,Wang Z G,Wu S D,Zhang Z F.Acta Mater,2009; 57:1586 |
[18] | Zhang P,An X H,Zhang Z J,Wu S D,Li S X,Zhang Z F,Figueiredo R B,Gao N,Langdon T G.Scr Mater,2012; 67:871 |
[19] | Murr L E.Interfacial Phenomena in Metals and Alloys.Massachuseas:Addison-Wesley Publishing Company,1975:142 |
[20] | Zhang Y,Tao N R,Lu K.Acta Mater,2011; 59:6048 |
[21] | Torre F D,Lapovok R,Sandlin J,Thomson P F,Davies C H J,Pereloma E V.Acta Mater,2004; 52:4819 |
[22] | Meyers M A,Chawla K K.Mechanical Behavior of Materials.2nd Ed.,Cambridge:Cambridge University Press,2009:337 |
[23] | McNelley T R,Swaminathan S,Su J Q.ScrMater,2008; 58:349 |
[24] | Jata K V,Semiatin S L.Scr Mater,2000; 43:743 |
[25] | Su J Q,Nelson T W,Sterling C J.JMater Res,2003; 18:1757 |
[26] | Feng A H,Ma Z Y.Acta Mater,2009; 57:4248 |
[27] | An X H,Wu S D,Zhang Z F,Figueiredo R B,Gao N,Langdon T G.ScrMater,2012; 66:227 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%