采用拉伸测试、TEM和电导率测试等方法,研究回归再时效(RRA)处理中预时效处理对喷射成形7075合金组织及性能的影响.结果表明,采用120℃,16h的欠时效预处理比120℃,24 h峰值时效预处理和120℃,32 h过时效预处理更有利于在回归处理过程中合金晶内析出相的回溶,比120℃,8h的早期预时效处理更有助于晶界相在再时效处理后断续分布.120℃,16h预时效处理的合金经RRA处理后,其抗拉强度和屈服强度分别为782和726 MPa,均高于T6峰值时效和常规回归再时效水平;电导率为22.7 MS/m,晶界析出相断续分布,合金抗腐蚀性能优良.
参考文献
| [1] | Wang Y Q,Wang Y,Chen P M,Shao Y W,Wang F H.Acta Metall Sin,2011; 47:455(王艳秋,王岳,陈派明,邵亚薇,王福会.金属学报,2011:47:455) |
| [2] | Marlaud T,Deschamps A,Bley F,Lefebvrec W,Baroux B.Acta Mater,2010; 58:248 |
| [3] | Marlaud T,Deschamps A,Bley F,Lefebvrec W,Baroux B.Acta Mater,2010; 58:4814 |
| [4] | George S L,Knutsen R D.JMater Sci,2012; 47:4716 |
| [5] | Su R M,Qu Y D,Li R X,Li R D.Appl Mech Mater,2012; 217:1835 |
| [6] | Jeyakumar M,Kumar S,Gupta G S.Mater Manuf Proc,2010; 25:777 |
| [7] | Silva G,Rivolta B,G-erosa R,Derudi U.J Mater Eng Perform,2013; 22:210 |
| [8] | Ricker R E,Lee E U,Taylor R,Lei C,Pregger B,Lipnickas E.Metall Mater Trans,2013; 44A:1353 |
| [9] | Ning A L,Liu Z Y,Feng C,Zeng S M.Acta Metall Sin,2006; 42:1253(宁爱林,刘志义,冯春,曾苏民.金属学报,2006; 42:1253) |
| [10] | Fooladfar H,Hasnemi B,Younesi M.JMater Eng Perform,2010;19:852 |
| [11] | Arnold E M,Schubbe J J,Moran P J,Bayles RA.J Mater Eng Perform,2012; 21:2480 |
| [12] | Cina B M.USPat,3856584,1974 |
| [13] | Li R D,Su R M,Qu Y D.J Mech Eng,2013; 49(20):22(李荣德,苏睿明,曲迎东.机械工程学报,2013; 49(20):22) |
| [14] | Su R M,Qu Y D,Li R D,Xie Q M,Wu Y S.Adv Mater Res,2013; 774:872 |
| [15] | Peng G,Chen K,Chen S,Fang H.Mater Sci Eng,2011; A528:4014 |
| [16] | Reda Y,Abdel-Karim R,Elmahallawi I.Mater Sci Eng,2008;A485:468 |
| [17] | Ohnishi T,Ibaraki Y,Ito T.Mater Trans JIM,1989; 30:601 |
| [18] | Higashi K,Ohnishi T,Tsukuda I.USPat,4713216,1987 |
| [19] | Lin J,Kersker M M.USPat,5108520,1992 |
| [20] | Han X L,Xiong B Q,Zhang Y A,Zhu B H,Li Z H,Li X W,Wang F,Liu H W.Chin JNonferrous Met,2012; 22:3006(韩小磊,熊柏青,张永安,朱宝宏,李志辉,李锡武,王锋,刘红伟.中国有色金属学报,2012;22:3006) |
| [21] | Islam M U,Wallace W.Mater Sci Technol,1983; 10:386 |
| [22] | Wang D,Ni D R,Ma Z Y.Mater Sci Eng,2008; A494:360 |
| [23] | Li G F,Zhang X M.Chin JNonferrous Met,2013; 23:1234(李国锋,张新明.中国有色金属学报,2013; 23:1234) |
| [24] | Jiang H,Faulkner R G.Acta Mater,1996; 44:1857 |
| [25] | Jiang H,Faulkner R G.Acta Mater,1996; 44:1865 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%