以4种不同Ni含量(15%~45%,原子分数)的新型γ'相强化Co-Al-W基合金为研究对象,通过时效与高温热处理显微组织分析以及显微硬度测试,研究了Ni对相转变温度、γ/γ'两相组织演变、γ'相高温溶解行为和显微硬度的影响.结果表明:随着Ni含量的增加,γ'相溶解温度升高,固相线温度未发生明显变化.4种合金经900℃,50 h热处理后,基体均为γ/γ'两相组织;随着Ni含量的增加,γ'相形貌由立方形逐渐向近似球形转变,γ'相体积分数不断降低.经300 h长时间热处理后,合金的γ'相形貌没有明显改变,γ'相体积分数出现不同程度的降低.对900℃,300 h热处理的合金进行970~1060℃高温处理后,γ'相体积分数随着热处理温度的升高而逐渐减少,并最终全部溶解而消失;低Ni含量(15%和25%)合金和高Ni含量(35%和45%)合金的γ'相形貌分别转变为球形和立方形.900℃,50h和300h显微硬度测试结果表明:随着Ni含量的增加,合金的硬度降低;热处理时间的延长使合金的硬度小幅增加.
参考文献
[1] | Sims C T,Stoloff N S,Hagel W C.Superalloys Ⅱ.New York:John Wiley & Sors,1987:135 |
[2] | Blaise J M,Viatour P,Drapier J M.Cobalt,1970; 49:192 |
[3] | Drapier J M,Coutsouradis D.Cobalt,1968; 39:63 |
[4] | Sato J,Omori T,Oikawa K,Ohnuma I,Karinuma R,Ishida K.Science,2006; 312(5770):90 |
[5] | Titus M S,Suzuki A,Pollock T M.In:Huron E S,Reed R C,Hardy M C,Mills M J,Montero R E,Portella P D,Telesman J eds.,Superalloys 2012,Champion,PA:TMS,2012:823 |
[6] | Titus M S,Suzuki A,Pollock T M.Scr Mater,2012; 66:574 |
[7] | Bauer A,Neumeier S,Pyczak F,Singer R F,G(o)ken M.Mater Sci Eng,2012; A550:333 |
[8] | Xue F,Wang M L,Feng Q.Mater Sci Forum,2011; 686:388 |
[9] | Xue F,Wang M,Feng Q.In:Huron E S,Reed R C,Hardy M C,Mills M J,Montero R E,Portella P D,Telesman J eds.,Superalloys 2012,Champion,PA:TMS,2012:813 |
[10] | Bauer A,Neumeier S,Pyczak F,G(o)ken M.Scr Mater,2010; 63:1197 |
[11] | Suzuki A,Pollock T M.Acta Mater,2008; 56:1288 |
[12] | Shinagawa K,Omori T,Sato J,Oikawa K,Ohnuma I,Kainuma R,Ishida K.Mater Trans,2008; 49:1474 |
[13] | Xue F,Zhou H J,Ding X F,Wang M L,Feng Q.Mater Lett,2013;112:215 |
[14] | Grosdidier T,Hazotte A,Simon A.Mater Sci Eng,1998; A256:183 |
[15] | Grosdidier T,Hazotte A,Simon A.Scr Metall Mater,1994; 30:1257 |
[16] | Cormier J,Jouiad M,Hamon F,Villechaise P,Milhet X.Philos MagLett,2010; 90:611 |
[17] | Omori T,Oikawa K,Sato J,Ohnuma I,Kattner U R,Kainuma R,Ishida K.Intermetallics,2013; 32:274 |
[18] | Xue F,Li Z Q,Feng Q.Mater Sci Forum,2010; 654-656:420 |
[19] | Li X H,Gan B,Feng Q,Sun z Q,Chen G L,Zhang G Q,Cao L M.J Univ Sci Technol Beijing,2008; 30:1369(李相辉,甘斌,冯强,孙祖庆,陈国良,张国庆,曹腊梅.北京科技大学学报,2008; 30:1369) |
[20] | Carroll L J,Feng Q,Pollock T M.Metall Mater Trans,2008;39A:1290 |
[21] | Carroll L J,Feng Q,Mansfield J F,Pollock T M.Metall Mater Trans,2006; 37A:2927 |
[22] | Murakumo T,Kobayashi T,Koizumi Y,Harada H.Acta Mater,2004; 52:3737 |
[23] | Shinagawa K,Omori T,Oikawa K,Kainuma R,Ishida K.Scr Mater,2009; 61:612 |
[24] | Jarrett R N,Tien J K.Metall Trans,1982; 13A:1021 |
[25] | Nathal M V,Ebert L J.Metall Trans,1985; 16A:1849 |
[26] | Viatour P,Drapier J M,Coutsouradis D.Cobalt,1973; 3:67 |
[27] | Chen M,Wang C Y.JAppl Phys,2010; 107:093705 |
[28] | Sponseller D L.In:Kissinger R D,Deye D J,Anton D L,Cetel A D,Nathal M V,Pollock T M,Woodford D A eds.,Superalloys 1996,Champion,PA:TMS,1996:259 |
[29] | Jiang W H,Guan H F,Hu Z Q.JAeron Mater,2001; 21(1):1(姜文辉,管恒荣,胡壮麒.航空材料学报,2001; 21(1):1) |
[30] | The Editorial Board of China Aeroautical Materials Handbook.China Aeronautical Matrials Handbook.2nd Ed.,Vol.2,Beijing:Standards Press of China,2002:531(《中国航空材料手册》编辑委员会.中国航空材料手册.第2版,第2卷,北京:中国标准出版社,2002:531) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%