Effects of Pulse Frequencies on Properties of MAO Coatings on Pure Titanium

LI Quan-Jun , WU Han-Hua , WANG Jian-Bo , GU Guang-Rui , JIN Zeng-Sun

Keywords： microarc oxidation , 脉冲频率 , 表面形貌 , 相组成

在Na₂CO₃-Na₂SiO₃电解液中, 利用微弧氧化技术在纯钛试样表面制备了氧化膜, 并研究了脉冲频率(500～8000Hz)对膜层生长、相组成及表面形貌的影响. 结果表明: 当脉冲频率<2000Hz时, 膜层的生长速率随频率增加迅速减小, 当>4000Hz时, 其生长速率几乎和频率无关. 微弧氧化膜主要由锐钛矿和金红石相TiO₂及少量不饱和氧化物TiO_2-x(0.022的相对含量与频率无关, 而TiO_2-x随频率的增加而逐渐减少. 氧化膜表面多孔, 随着频率的增加, 膜表面的粗糙度和微孔尺寸逐渐减小, 而微孔的密度逐渐增加.

Microarc oxidation coatings were prepared on pure titanium substrates in a Na₂CO₃ and Na₂SiO₃ electrolytic solution by microarc oxidation with the pulse frequency of 500～8000Hz, the effects of pulse frequencies on growth kinetics, surface morphology and phase composition of the coatings were studied.
The result shows that the coating growth rate is dependent on the pulse
frequency. When the frequency is less than 2000Hz, with the increase of frequencies, the coating growth rate decreases sharply, while the frequency is greater than 4000Hz, it keeps almost invariable with the treating frequency increased. The coatings consist of plentiful rutile and anatase, and a small quantity of unsaturated oxideTiO_2-x, (0.022-x reduces gradually with the increase of the frequency. The coating surface is porous, with the frequency increasing, the roughness and micropore size of the coating surface decrease gradually, and the pore number increases little by little.