以β-磷酸三钙/硅酸钙(β-TCP/CS)纳米复合粉体为原料, 制备了质量比为50:50的β-TCP/CS复合生物陶瓷. 研究表明, 1150℃烧结5h得到的样品强度最好, 其致密度>96%, 晶粒尺寸约120nm, 强度达126MPa、同人体致密骨相当; 复合陶瓷在模拟体液中浸泡1天表面就全部被类骨羟基磷灰石层覆盖住, 28天的降解率达10.1%, 具有良好的生物活性和降解性. 研究结果显示β-TCP/CS复合生物陶瓷有望作为强度较好的可降解生物活性硬组织修复材料.
β-Ca 3(PO 4) 2/CaSiO 3 (β-TCP/CS) composite bioceramics with weight ratio of 50:50 were fabricated by using the β-TCP/CS nano-composite powders. The β-TCP/CS composite bioceramics with >96% relative density and 120nm grain size were obtained after sintering at 1150℃ for 5h. The bending strength of the samples reached about 126MPa, which was similar to those of the human cortical bone. After soaking in simulated body fluid for 1 day, the samples were completely covered wity hydroxyapatite layers. The degradability of the
samples reached 10.1% within 28 days in~ vitro. The results suggest excellent
in~ vitro bioactivity and degradability of the β-TCP/CS composite
bioceramics. Therefore, these β-TCP/CS composite bioceramics may be
potential candidates as good mechanical strength, bioactive and degradable
biomaterials for hard tissue repair applications.
参考文献
[1] | Klein C P A T, Groot K K D, Drissen A A, it et al. Biomaterials, 1985, 6 (3): 189--192. [2] Hench L L. it J. Am. Ceram. Soc., 1991, 74 (7): 1487--1510. [3] 钟吉品, Hench L L(ZHONG Ji-Pin, {it et al). 无机材料学报(Journal of Inorganic Materials), 1995, 10 (2): 129--138. [4] Hench L L, Xynos I, Edgar A, it et al. 无机材料学报(Journal of Inorganic Materials), 2002, 17 (5): 897--909. [5] Siriphannon P, Hayashi S, Yasumori A, it et al. J. Mater. Res., 1999, 14 (2): 529--536. [6] Liu X Y, Ding C X, Chu P K. it Biomaterials, 2004, 25 (10): 1755--1761. [7] Lin K L, Chang J, Zhai W Y, it et al. Ceram. Intern., 2005, 31 (2): 323--326. [8] 林开利, 常江, 汪正.无机材料学报(Journal of Inorganic Materials), 2005, 20 (3): 692--698. [9] Xue W C, Liu X Y, Zheng X B, it et al. Biomaterials, 2005, 26 (17): 3455--3460. [10] Xynos I D, Edgar A J, Buttery L D, it et al. J. Biomed. Mater. Res., 2001, 55 (2): 151--157. [11] PN De Aza, Guitiacute{ an F, S De Aza. it Acta. Materialia, 1998, 46 (7): 2541--2549. [12] PN De Aza, Guitiacute{ an F, S De Aza. it Biomaterials, 1997, 18 (19): 1285--1291. [13] 黄翔. 中国科学院上海硅酸盐研究所博士论文: 生物活性硅灰石及其复合材料的研究, 2002. [14] Huang X, Jiang D L, Tan S H. it J. Biomed. Mater. Res., 2004, 69B (1): 70--72. [15] Cho S B, Nakanishi K, Kokubo T, it et al. J. Am. Ceram. Soc., 1995, 78 (7): 1769--1774. [16] Elliott J C. Structure and Chemistry of the Apatites and Other Calcium Orthophosphates, Amsterdam: Elsevier, 1994. [17] Hoeie D, Zussman. Chain Silicates, Longman, London, 1963. |