用热压工艺制备了AlN-BN复合陶瓷材料, 研究了不同含量CaF2烧结助剂对致密化、介电和热导性能的影响. 研究表明: CaF2添加剂可促进材料致密化, 净化材料晶界, 优化材料的综合性能. 热压1850℃保温3h可获得高致密度的烧结体, 添加3wt%~4wt%的CaF2, 可获得98.53%~98.54%的相对密度. 制备的AlN-BN复合材料其介电常数在7.29~7.60之间, 介电损耗值最小为6.28×10-4, 添加3wt%的CaF2获得的热导率为10W·m-1·K-1.
A series of samples of AlN-BN ceramic composites with different contents of sintering additives CaF2(0-4wt%) were prepared by hot-pressing in nitrogen atmosphere at 1850℃ for 3h. The effects of sintering additives on densification, dielectric properties and thermal conductivity of AlN-BN composites were explored. The addition of CaF2 results in improvements in the level of densification and purified the grain boundary. AlN-BN composites with relative density of 98.53%-98.54% are obtained when CaF2 contents are 3wt%-4wt%. Dielectric constants of samples are between 7.29 and 7.60 and the best tanδ value is 6.28×10-4. It is found that dielectric constants increase with the increasing CaF2 contents and depend on the density of
the AlN-BN ceramic composites. The highest thermal conductivity reach 110W·m-1·K-1 by adding 3wt% CaF2.
参考文献
[1] | |
[2] | Shoichi Kume, Masaki Yasuoka, Naoki Omura, et al. International Journal of Refractory Metals & |
- 下载量()
- 访问量()
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%