采用固相法制备了(1-x)CaTiO3-x(Li1/2Sm1/2)TiO3系列微波介质陶瓷材料, 研究了该体系的相组成、烧结性能和微波介电性能之间的关系. 结果表明: 在x=0.1~0.9mol范围内, (1-x)CaTiO3-x(Li1/2Sm1/2)TiO3
体系均形成了单一的斜方钙钛矿结构; x=0.1~0.5和x=0.6~0.9组分的最佳烧结温度分别为1250和1300℃; 介电常数εr、无载品质因数与谐振频率乘积Qf值、谐振频率温度系数τf均随着x的增大而减小. 当x=0.7时, 1300℃下保温5h烧结得到的材料的微波介电性能为: εr=116.5, Qf=3254GHz, τf=42.43×10-6/℃.



(1-x)CaTiO3-x(Li1/2Sm1/2)TiO3 microwave dielectric ceramics were prepared by solid sate reaction technique. The crystal structure, sintering properties and microwave dielectric properties of the ceramics were investigated. The results show that a single orthorhombic perovskite structure forms in the x range from 0.1 to 0.9; the best sintering temperatures of (1-x)CaTiO3-x(Li1/2Sm1/2)TiO3 are 1250℃ and 1300℃ in the x range from 0.1 to 0.5 and 0.6 to 0.9, respectively; the dielectric constant εr, the product of quality factor and resonance frequency (Qf ) value and the temperature coefficient of resonant frequency τf decrease with the increasing of x. The Ca0.3(Li1/2Sm1/2)0.7TiO3 ceramic sintered at 1300℃ for 5h exhibits excellent microwave dielectric properties: εr=116.5, Qf=3254GHz, τf=42.43×10-6/℃.



参考文献

[1] 杨辉, 张启龙, 王家邦, 等. 硅酸盐学报, 2003, 31 (10): 965--973.
[2] Kell R C, Greenham A C, Olds G. C E. J. Am. Ceram. Soc., 1973, 56 (7): 352--354.
[3] Takahashi H, Baka Y, Ezaki K, et al. Jpn. J. Appl. Phys., 1991, 30 (9B): 2339--2342.
[4] Shannon R D. Acta Cryst., 1976, A32: 751--767.
[5] Eung S K, Ki H Y. J. Eur. Ceram. Soc., 2003, 23 (14): 2397--2401.
[6] 吕文中, 张道礼, 黎步银, 等. 功能材料, 2000, 31 (6): 572--575.
[7] Nenasheva E A, Kartenko Artenko N F. J. Eur. Ceram. Soc., 2001, 21 (15): 2697--2701.
[8] 何进, 杨传仁. 电子元件与材料, 1995, 14 (2): 7--13.
[9] Kajfea D. J. Eur. Ceram. Soc., 2001, 21 (15): 2663--2667.
[10] Reaner I M, Wise P, Ubic R, et al. Philosophical Magazine A, 2001, 81 (2): 501--510.
[11] 陆栋, 蒋平, 徐至中. 固体物理
学. 第一版. 上海: 上海科学技术出版社, 2003. 245--246.
[12] Colla E L, Reaney I M, Setter N. Jpn. J. Appl. Phys., 1993, 74 (5): 3414--3418.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%