以氧化石墨(GO)为主体, 苯胺-邻甲氧基苯胺导电共聚物(P(An-co-oAs))为客体, 采用剥离/重新组装技术合成出P(An-co-oAs)嵌入GO复合材料. FTIR分析显示, P(An-co-oAs)的N-H基团与GO片层中的C=O基团存在着氢键作用. XRD和TEM分析表明, P(An-co-oAs)/GO保持良好的层状结构, 且随着P(An-co-oAs)含量的增加, 复合材料的层间距不断扩大. P(An-co-oAs)的插入, 使得复合材料的室温电导率比GO提高2～3个数量级. 同时发现, 增加P(An-co-oAs)的含量, 不仅提高了GO的电化学活性, 也改善了GO的锂离子嵌入/脱嵌的循环稳定性.
Aniline/o-anisidine copolymer (P(An-co-oAs)) intercalated graphite oxide (GO) composites were synthesized through the delamination/reassembling method using GO as host and conducting P(An-co-oAs) as guest. FTIR spectra indicate that the hydrogen bonds are formed between the amino groups of P(An-co-oAs) and the carbonyl groups on the internal layers of GO. XRD and TEM results show that the P(An-co-oAs)/GO composites maintain good lamellar structure, and the interlayer spacing of GO is enlarged with the increase of the added amount of P(An-co-oAs). The electrical conductivity of the composites is 2 to 3 orders of magnitude higher than that of the GO. The intercalation of P(An-co-oAs) also has a pronounced effect on the electrochemical properties of the GO.
参考文献
| [1] | Wu C G, DeGroo D C, Marcy H O. Chem. Mater., 1996, 8 (8): 1992--2004. [2] Leroux F, Goward G, Power W P. J. Electrochem. Soc., 1997, 144 (11): 3886--3895. [3] Wu C G, DeGroot D C, Marcy H O, et al. J. Am. Chem. Soc., 1995, 117 (12): 9229--9242. [4] Huguenin F, dos Santos D S, Bassi A, et al. Adv. Funct. Mater., 2004, 14 (10): 985--991. [5] Li Z F, Ruckenstein E. Langmuir, 2002, 18 (18): 6956--6961. [6] Huguenin F, Torresi R M, Buttry D A. J. Electrochem. Soc., 2002, 149 (5): A546--553. [7] Zhao J, Wang G C, Li X W, et al. J. Appl. Polym. Sci., 2007, 103 (4): 2569--2574. [8] Higashika S, Kimura K, Matsuo Y, et al. Carbon, 1999, 37 (2): 351--358. [9] Liu Z H, Wang Z M, Yang X, et al. Langmuir, 2002, 18 (12): 4926--4932. [10] Liu P, Gong K, Xiao P, et al. J. Mater. Chem., 2000, 10 (4): 933--935. [11] Matsuo Y, Hatase K, Sugie Y. Chem. Mater., 1998, 10 (8): 2266--2269. [12] 刘平桂, 龚克成. 高分子学报, 2000, (4): 492--495. [13] Cassagneau T, Fendler J H. Adv. Mater., 1998, 10 (11): 877--881. [14] Wang G C, Yang Z Y, Li X W, et al. Carbon, 2005, 43 (12): 2564--2570. [15] Cao Y, Andriatta A, Heeger A J, et al. Polymer, 1989, 30 (12): 2305--2311. [16] Hummers W S, Offeman R E. J. Am. Chem. Soc., 1958, 80 (6): 1339. [17] Sasaki T, Watanabe M. J. Am. Chem. Soc., 1998, 120 (19): 4682--4689. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%