为在炭/炭复合材料表面制备C/SiC浓度梯度高温抗氧化涂层,预先用料浆涂刷-高温处理工艺在其表面制备了预炭层.借助XRD、Raman和SEM等测试手段对所制备预炭层的组织结构和微观形貌进行了表征,讨论了不同的原料配比和炭化温度对预炭层结构的影响,并对预炭层与基体的结合性能进行了测定.研究结果表明:制备的预炭层结构致密,与基体具有较好的结合性能,其结合强度可达10.95MPa.不同的原料配比和炭化温度影响了炭层序态结构的形成,最终形成了不同结构的预炭层.
Pre-coated carbon layers on the surface of carbon/carbon composites were prepared firstly by slurry and high-temperature treatment for preparing the anti-oxidation coating with SiC concentration gradient. The micrographs and microstructures of the pre-coated carbon layer were characterized by SEM, Raman and XRD. The effects of different graphite content and carbonization temperature on the microstructure of pre-coated carbon layer were investigated. The bonding strength between the carbon layer and the C/C composites was also measured. The results show that the as-prepared carbon layer is dense and the bend strength reaches 10.5MPa. The structures of the pre-coated carbon layer are influenced by the graphite content and carbonization temperature, and the pre-coated carbon layers with different structures are obtained.
参考文献
[1] | ]Buckley J D. Am. Cerm. Soc. Bull., 1988, 67(2): 364-368. [2]李贺军. 新型炭材料, 2001, 16(2): 79-80. [3]孙万昌, 李贺军, 白瑞成, 等(SUN Wan-Chang, et al). 无机材料学报(Journal of Inorganic Materials), 2005, 20(3): 671-676. [4]Westwood M E, Webster J D, Day R J, et al. J. Mater.Sci., 1996, 31(6): 1389-1397. [5]Strife J, Sheehan J. Ceramic. Bulletin., 1988, 67(2): 369-374. [6]Fu Q G, Li H J, Shi X H, et al. Scripta materialia, 2005, 52(9): 923-927. [7]王 标, 李克智, 李贺军, 等(Wang Biao, et al). 无机材料学报(Journal of Inorganic Materials), 2007, 22(4): 737-741. [8]牛晓滨,廖 源,常 超,等(NIU Xiao-Bin, et al).无机材料学报(Journal of Inorganic Materials),2004, 19(2): 397-402. [9]Huang J F, Zeng X R, Li H J, et al. Carbon, 2004, 42(8-9):1517-1521. [10]曾燮榕, 李贺军, 杨 峥, 等. 金属热处理学报, 2000, 21(2): 64 -67. [11]Ueda T, Morimoto T, Kumagai H, et al. Carbon, 1995, 33(1): 73-78. [12]Zhang Y L, Li H J, Fu Q G, et al. Surf.Coat. Technol., 2006, 201(6): 3491-3495. [13]Wu T M, Won K H, Wei W C. Surf.Coat. Technol., 1996, 78(1): 64-71. [14]Smeacetto F, Ferraris M, Salvo M. Carbon, 2003, 41(11):2105-2111. [15]Zhang Y L, Li H J, Fu Q G, et al. Carbon, 2008, 46 (1): 179-182. [16]李崇俊, 马伯信, 金志浩. 新型炭材料 , 2001, 16(1): 19-24. [17]汪树军, 刘庆国. 北京科技大学学报, 2000, 22(6): 889-892. [18]王君林, 关振中. 材料科学与工艺, 1995, 3(4): 39-43. [19]Li X K, Liu L, Shen S D, et al. New Carbon Materials., 2000, 15(3): 52-54. |
- 下载量()
- 访问量()
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%