为提高陶瓷喷砂嘴抗冲蚀磨损能力,缓解喷嘴入口、出口的高应力状态,采用热压烧结工艺制备了Al2O3+(W,Ti)C/Al2O3+TiC三层对称型叠层陶瓷材料及叠层陶瓷喷嘴.研究结果表明:叠层陶瓷材料表层较之相应单一材料而言,具有更高的硬度和断裂韧性;在相同的冲蚀磨损条件下,叠层陶瓷喷嘴的抗冲蚀磨损性能较非叠层陶瓷喷嘴有显著的提高;试验分析叠层陶瓷喷嘴的最佳层厚比为2.此外,采用有限元法对叠层陶瓷喷嘴在制备过程中的残余应力进行了理论计算,给出了叠层陶瓷喷嘴中残余应力与层厚比的关系.研究表明,残余压应力的存在,细化了晶粒,提高了叠层材料表层的硬度和断裂韧性,是叠层陶瓷喷嘴其抗冲蚀磨损能力提高的原因.理论分析最佳层厚比也为2,理论分析与试验结果相互印证.
参考文献
| [1] | Deng Jianxin,Liu Lili,Ding Mingwei.Materials and Design,2007,28(7):2099-2105. |
| [2] | 李国英主编.表面工程手册.北京:机械工业出版社,1998.21-27. |
| [3] | Deng Jianxin,Liu Lili,Ding Mingwei.Materials characterization,2008,59(1):1-8. |
| [4] | Ding Zeliang,Deng Jianxin,Li Jianfeng.Materials & Design,2007,28(5):1531-1538. |
| [5] | Ding Zeliang,Deng Jianxin,Zen Xiaohong,et al.International Journal of Refractory Metals and Hard Materials,2008,26(4):334-339. |
| [6] | 冯益华.新型陶瓷喷砂嘴的研究开发及其冲蚀磨损机理研究.山东大学博士论文,2003. |
| [7] | Deng Jianxin,Feng Yihua,Ding Zeliang.Journal of the European Ceramic Society,2003,23(2):323-329. |
| [8] | 刘莉莉,邓建新,皇攀凌,等.中国科学(E辑),2007,37(7):8571-865. |
| [9] | Deng Jianxin,Wu Fengfang,Zhao Jinlong.Internaltional Journal of Machine Tools and Manufacture,2007,47(12-13):2031-2039. |
| [10] | Deng Jianxin,Zhang Xihua,Niu Pingzhang,et al.Tribology International,2006,39(3):274-280. |
| [11] | Toschi F,Melandri C,Pinasco P,et al.Journal of American Ceramic Society,2003,86(9):1547-1553. |
| [12] | 苏盛彪,包亦望,杨建军.硅酸盐学报,2003,31(8):743-747. |
| [13] | Tekmen C,Ozdemir I,Celik E.Surface and Coatings Technology,2003:174-175:1101-1105. |
| [14] | Portu de G,Micele L,Pezzotti G.Composites Part B:Engineering,2006,37(6):556-567. |
| [15] | Lambrinou K,Lauwagie T,Chalvet E,et al.Journal of the European Ceramic Society,2007,27(2-3):1307-1311. |
| [16] | Deng Jianxin,Liu Lili,Li Jianfeng,et al.International Journal of Refractory Metals and Hard Materials,2007,25(2):130-137. |
| [17] | de Portu G,Micele L,Prandstraller D,et al.Wear,2006,260(9-10):1104-1111. |
| [18] | Li Dongyun,Qiao Guanjun,Jin Zhihao.Ceramics International,2004,30(2):213-217 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%