获得多功能单一过渡层是简化涂层导体多层结构的主要课题之一. 采用化学溶液方法制备La掺杂CeO_2过渡层,研究La掺杂量对CeO_2薄膜表面形貌和双轴取向生长的影响. 结果表明La掺杂量为10mol%的薄膜表面平整致密,且能保持锐利的双轴织构. 通过多次涂敷工艺,获得具有120nm厚的Ce_0.9La_0.1O_2过渡层. 采用脉冲激光沉积方法在Ce_(0.9)La_(0.1)O_2/NiW结构模板层上沉积了YBCO超导薄膜,其起始临界转变温度达到90.5K. 这表明采用化学溶液方法制备Ce_(0.)9La_(0.1)O_2薄膜是一种有前景的简化涂层导体多层结构的方法.
Developing multi-functional single buffer layer is one of the most important challenges for simplification of coated conductors configuration. La-doped CeO_2 films were prepared by chemical solution method. And surface morphology and texture quality of the La-doped CeO_2 films were investigated in details. The results show that the as-obtained pore-free Ce_(0.9)La_(0.1)O_2 film are epitaxially deposited on the textured NiW substrate. The 120nm thickness Ce_(0.9)La_(0.1)O_2 film is obtained though multi-coating route. The YBCO film with T_(co)=90.5K, which is deposited on Ce_(0.9)La_(0.1)O_2/NiW metallic template by PLD method. It suggects that Ce_(0.9)La_(0.1)O_2 film prepared by chemical solution route have a promising prospect for the simplification of coated conductors configuration.
参考文献
| [1] | Andrea Cavallaro,Felip Sandiumenge,Jaume Gàzquez,et al.Adv.Funct.Mater.2006,16(10):1363-1372. |
| [2] | Coll M,Gazquez J,Sandiumenge F,et al.Nanotechnology,2008,19(39):395601-1-7. |
| [3] | Xu Yongli.High Jc Epitaxial YBCO Films through a Non-fluorine Approach for CCs Application.OhiO:PhD Dissertation of University of Cincinnati,2003. |
| [4] | Bhuiyan M S,Paranthaman M,Sathyamurthy S,et al.Supercond.Sci.Technol.,2003,16(11):1305-1309. |
| [5] | Yasuhiro Iijima,Kazuomi Kakimoto,Yasunori Sutoh,et al.IEEE Trans.Appl.Supercond.,2003,15(2):2590-2594. |
| [6] | Gianni L,Baldini A,Bindi M,et al.Physica C,2005,426-431(part 2):872-877. |
| [7] | Bhuiyan M S,Paranthaman K,Salama K.Supercond.Sci.Technol.,2006,19(2):R1-R12. |
| [8] | Stewart E,Bhuiyan M S,Sathyamurthy S,et al.Materials Research Bulletin,2006,41(6):1063-1068. |
| [9] | Zhao Yue,Suo Hongli,Zhang Yingxiao,et al.IEEE Transactions on Applied Superconductivity,2007,17(2):1-7. |
| [10] | 周岳亮,赵唯义.物理,1999,21(1):17-24. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%