按组成Li0.35Zn0.30Fe2.29MnxO4-δ+0.005mol%Bi2O3和Li0.35Zn0.30Fe2.29O4-δ+0.005mol%Bi2O3+x/3mol%Mn3O4(x=0.02～0.08)在920和950℃制备缺铁LiZn铁氧体,分别在原料和预烧料中添加Mn3O4.结果表明:920℃烧结时,在原料中添加适量Mn3O4可提高样品饱和磁化强度Ms和剩磁Br,降低矫顽力Hc,而在预烧料中添加Mn3O4对Ms和Br影响不大,不完全固相反应导致两种样品Hc很高,但在原料中添加Mn3O4的样品Hc相对较低.950℃烧结时,两组样品Hc均大幅下降,但在原料中添加Mn3O4的样品Hc反而相对较高.两种方式添加Mn3O4均可提高电阻率ρ,x=0.06时ρ出现峰值,且在原料中添加Mn3O4的样品ρ较高.
参考文献
| [1] | Pardavi-Horvath M.J.Magn.Magn.Mater.,2000,215-216(6):171-183. |
| [2] | Baba P D,Argentina G M,Courtney W E,et al.IEEE Trans.Magn.,1972,MAG-8(1):83-94. |
| [3] | Liu C Y,Lan Z W,Jiang X N,et al.J.Magn.Magn.Mater.,2008,320(7):1335-1339. |
| [4] | 余忠,陈代中,兰中文,等(YU Zhong,et al).无机材料学报(Journal of Inorganic Materials),2007,22(6):1173-1177. |
| [5] | Teo M L S,Kong L B,Li Z W,et al.J.Alloy.Compd.,2008,459(1/2):557-566. |
| [6] | Han Z Q,Liao Y,Feng T.Densification,Solid Reaction and Properties of Low Temperature Sintered LiZn Ferrites Prepared by Ceramics Method.ICF10.Chengdu,2008:336-338. |
| [7] | Jiang X N,Lan Z W,Yu Z,et al.Effects of Sintering Temperature and Bi2O3 on Li Volatilization in LiZn Ferrites.ICF10.Chengdu,2008:364-367. |
| [8] | 都有为.铁氧体.南京:江苏科学技术出版社,1996:49-53. |
| [9] | 王会宗.磁性材料及其应用,北京:国防工业出版社,1989:288-289. |
| [10] | White G O,Patton C E.J.Magn.Magn.Mater.,1978,9(4):299-317. |
| [11] | 陈代中.低温制备低矫顽力LiZn铁氧体材料研究.成都:电子科技大学硕士论文,2006. |
| [12] | 宛德福,马兴隆.磁性物理学.北京:电子工业出版社,1999:374-378. |
| [13] | 黄永杰,李世堃,兰中文.磁性材料.成都:电子科技大学出版社,2002:1-5. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%