采用电弧熔炼法和放电等离子体烧结法,制备了稀土掺杂的金属间化合物Zr1-xLaxNiSn(x=0.05,0.1,0.15,0.2,0.3,0.4)和Zr0.98R0.0202NiSn0.98X0.02(R=La,Ce;X=Sb,Bi).用X射线衍射仪分析研究了它们的晶体结构随稀土替代量演化的规律.在室温到700 K的范围内,对其热电特性进行了评价.研究结果表明,代换量x小于0.15时,稀土原子可以进入晶格形成单相化合物.代换量x大于0.15的样品中含有非half-Heusler的第二相,且含量随x增大而增加.少量稀土掺杂可以有效地降低材料的热导率而保持良好的电输运特性.在575 K,Zr0.98La0.02NiSn0.98Sb0.02的热电优值达到0.5.
参考文献
| [1] | Muta H,Yamaguchi T,Kurosaki K,et al.Thermoelectric Properties of ZrNiSn Based Half-Heusler Compounds.1CT Proceedings,IEEE 2005:339-342. |
| [2] | 黄向阳,徐政,陈立东(HUANO Xiang-Yang,et al).Half-Heusler热电半导体材料.无机材料学报(Journal of Inorganic Materials),2004,19(1):25-30. |
| [3] | Muta H,Kanemitsu T,Kurosaki K,et al.High-temperature thermoelectric properties of Nb-doped MNiSn (M=Ti,Zr) half-Heusler compound.Journal of Alloys and Compounds,2009,469(1/2):50-55. |
| [4] | Culp S R,Poon S J,Hickman N,et al.Effect of substitutions on the thermoelectric figure of merit of half-Heusler phases at 800℃.Applied Physics letters,2006,88(4):042106-1-3. |
| [5] | Kim S,Kimura Y,Mishima Y.High temperature thermoelectric properties of TiNiSn-based half-Heusler compounds.Intermetallics,2007,15(3):349-356. |
| [6] | Kim S W,Kimura Y,Mishima Y.Enhancement of high temperature thermoelectric properties of intermetallic compounds based on a Skutterudite IrSb3 and a half-Heusler TiNiSb.Science and Technology of Advanced Materials,2004,5(4):485-489. |
| [7] | Culp S,Poon S J,Sorloaica N,et al.Complex MNiSn Phases as Stable High-temperature Thermoelectric Materials.ICT Proceedings,IEEE,2005:387-390. |
| [8] | Shen Q,Zhang L M,Chen L D,et al.Thermoelectric properties of ZrNiSn-based half-Heusler compounds by solid state reaction method.Journal of Materials Science Letters,2002,20(24):2197-2199. |
| [9] | Sakurada S,Shutoh N.Effect of Ti substitution on the thermoelectric properties of (Zr,Hf) NiSn half-Heusler compounds.Applied Physics Utters,2005,86(8):082105-1-3. |
| [10] | MorimuraT,HasakaM,Kondo S.Transmission election microscopy observation of the half-Heusler compound Ti0.5(Zr0.5Hf0.5)0.5NiSn0.998Sb0.002.Scripta Materialia,2008,59(8):886-888. |
| [11] | Katsuyama S,Matsuo R,Ito M.Thermoelectric properties of half-Heusler alloys Zr1-xYxNiSn1-ySby.Journal of Alloys and Compounds,2007,428(1/2):262-267. |
| [12] | Culp S R,Simonson J W,Poon S J,et al.(Zr,Hf)Co(Sb,Sn) half-Heusler phases as high-temperature (》700 ℃) p-type thermoelectric materials.Applied Physics Letters,2008,93(2):022105-1-3. |
| [13] | Xia Y,Bhattacharya S,Ponnambalam V,et al.Thermoelectric properties of semimetallic (Zr,Hf)CoSb half-Heusler phases.Journal of Applied Physics,2000,88(4):1952-1955. |
| [14] | Mastronardi K,Young D,Wang C C,et al.Antimonides with the half-Heusler structure:new thermoelectric materials.Applied Physics Letters,1999,74(10):1415-1417. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%