将纳米ZrO2-8wt%Y2O3和纳米ZrO2-8wt%Y2O3中掺杂25wt%纳米CeO2(CeO2/ZrO2-8wt%Y2O3)的两种粉末进行团聚处理,用等离子喷涂方法在GH30高温合金表面分别制备了两种材料热障涂层.用扫描电镜、透射电镜和X射线衍射仪对掺杂了25wt%纳米CeO2的团聚体粉末和涂层的微观组织结构进行分析研究,测试比较了两种涂层在900、1100和1300℃时的热震性能,并试验了两种涂层在1050℃、保温100h后的抗氧化能力.结果表明,纳米粉末经团聚处理后为多孔的球形结构,掺杂纳米CeO2涂层组成相为稳定的t相(t-ZrO2、t-Zr0.82Y0.18O1.91、t-Zr0.82Ce0.8O2)和c相(c-CeO2),并保持纳米组织结构,平均晶粒尺寸为45nm,其抗热震性能和氧化性能要高于纳米ZrO2-8wt%Y2O3涂层.
参考文献
[1] | Schulz U,Leyens C,Fritscher K.Some recent trends in research and technology of advanced thermal barrier coatings.Aerospace Science and Technology,2003,7(1):73-80. |
[2] | Evans A G,Mumm D R,Hutchinson J W,et al.Mechanisms controlling the durability of thermal barrier coatings.Progress in Materials Science,2001,46(5):505-553. |
[3] | DeMasi-Marcin J T,Gupta D K.Protective coatings in the gas turbine engine.Surface and Coatings Technology,1994,68-69:1-9. |
[4] | Lima R S,Kucuk A,Berndt C C.Integrity of nanostructured partially stabilized zirconia after plasma spray processing.Materials Science and Engineering A,2001,313(1/2):75-82. |
[5] | Wang W Q,Sba C K,Sun D Q,et al.Microstructural feature,thermal shock resistance and isothermal oxidation resistance of nanostructured zirconia coating.Materials Science and Engineering A,2006,424(1/2):1-5. |
[6] | Chen H,Ding C X.Nanostructured zirconia coating prepared by atmospheric plasma spraying.Surface and Coatings Technology,2002,150(1):31-36. |
[7] | 陈煌,林新华,曾毅,等(CHEN Huang,et al).热喷涂纳米陶瓷涂层研究进展.硅酸盐学报(Journal of the Chinese Ceramic Society),2002,30(2):235-239. |
[8] | 陈煌,周霞明,黄民辉,等(CHEN Huang,et al).纳米ZrO2等离子涂层的结构,性能和工艺特点.无机材料学报(Journal of Inorganic Materials),2003,18(4):911-916. |
[9] | 陈煌,丁传贤(CHEN Huang,et al).等离子喷涂氧化锆纳米涂层显微结构研究.无机材料学报(Journal of Inorganic Materials)2002,17(4):882-886. |
[10] | 梁波,丁传贤(LIANG Bo,et al).氧化锆纳米等离子涂层的结构与热震性能研究.无机材料学报(Journal of Inorganic Materials),2006,21(1):250-256. |
[11] | Kear B H,Skandan G.Theraml spray processing of nanoscale materials.Nanostructure Materials,1997,8(6):765-769. |
[12] | Park S Y,Kim J H,Kim M C,et al.Microscopic observation of degradation behavior in yttria and ceria stabilized zirconia thermal barrier coatings under hot corrosion.Surface Coatings & Technology,2005,190(2/3):357-365. |
[13] | Lee C H,Kim H K,Choi H S,etal.Phase transformation and bond coat oxidation behavior of plasma-sprayed zirconia thermal barrier coating.Surface Coatings and Technology,2000,124(11):1-12. |
[14] | Huang P J,Swab J J,Patel P J,et al.Evaluation of CeSZ Thermal Barrier Coatings for Diesels.Proceedings of the 1st International Thermal Spray Conference,ASM International,Materials Park,OH,Canada,2000:1179-1182. |
[15] | Choi Hanshin,Kim Hyungjun,Lee Changhee.Phase evolution of plasma sprayed ceria and yttria stabilized zirconia thermal barrier coating.Journal of Materials Science Letters,2002,21(17):1359-1361. |
[16] | Cao X,Vassen R,Fischer W.Lanthanum-cerium oxide as a thermal barrier-coating material for high-temperature applications.Advanced Materials,2003,15(17):1438-1442. |
[17] | Lima R S,Kucuka A,Berndt C C.Evaluation ofmicro-hardness and elastic modulus of thermally sprayed nanostructured zirconia coatings.Surface and Coatings Technology,2001,135(2/3):166-172. |
[18] | Khor K A,Gu Y W,Dong Z L.Properties of Plasma Sprayed Functionally Graded YSZ/NiCoCrA1Y Composite Coatings.Proceedings of the 1st International Thermal Spray Conference,ASM Inemational,Materials Park,OH,Canada,2000:1241-1247. |
[19] | Scrivani A,Bardi U.On the Experimental Correlation Between Plasma Spray Process Conditions and Yttria Partially Stabillized Zirconia Coatings Properties.Proceedings of the 1st International Thermal Spray Conference,ASM Inernational,Materials Park,OH,Canada,2000:1207-1210. |
[20] | Cole M A,Walker R.High Temperature Erosion Properties of Thermal Barrier Coatings Produced by Acetylene Sprayed High Velocity Oxygen Fuel Process.Proceedings of the 1st International Thermal Spray Conference,ASM Inernational,Materials Park,OH,Canada,2000:1191-1200. |
[21] | Gleiter H.Nanocrystalline materials.Progress in Materials Science,1989,33(4):223-315. |
[22] | Gupta K T,Bechtold J H,Kuznicki R C,et al.Stabilization of tetragonal phase in polycrystalline zirconia.Journal of Material Science,1977,12(12):2421-2426. |
[23] | Gong W B,Sha C K,Sun D Q,et al.Microstructures and thermal insulation capability of plasma-sprayed nanostructured ceria stabilized zirconia coatings.Surface & Coatings Technology,2006,201(6):3109-3115. |
[24] | Wright P K,Evans A G Mechanisms governing the performance of thermal barrier coatings.Current Opinion in Solid State and Materials Science,1999,4(3):255-265. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%