以可溶性的草酸铌为前体,通过聚合络合法合成了可见光响应光催化剂K4Ce2Nb10O30.XRD、SEM、BET以及UV-Vis等表征结果表明:通过该法制备的光催化剂相对于传统高温固相反应法制备的样品具有更小(20~50nm)且分布均匀的纳米颗粒和较高的比表面积.在可见光下(λ>400 nm)分解水的活性测试中,聚合络合法获得K4Ce2Nb10O30比高温固相样品具有更高的光催化分解水活性,并且在紫外光段下(λ>300 nm)具备了完全分解纯水的光催化活性.
参考文献
[1] | Ravelli D,Dondi D,Fagnoni M,et al.Photocatalysis:a multi-faceted concept for green chemistry.Chem.Soc.Rev.,2009,38(7):1999-2011. |
[2] | Kitano M,Hara M.Heterogeneous photocatalytic cleavage of water.J.Mater.Chem.,2010,20(4):627-641. |
[3] | Woodhouse M,Parkinson B A.Combinational approaches for the identification and optimization of oxide semiconductors for efficient solar photoelectrolysis.Chem Soc.Rev.,2009,38:197-210. |
[4] | Kudo A,Miseki Y.Heterogeneous photocatalyst materials for water splitting.Chem.Soc.Rev.,2009,38(1):253-278. |
[5] | Maeda K,Xiong A,Yoshinaga T,et al.Photocatalystic overall water splitting promoted by two different cocatalysts for hydrogen and oxygen evolution under visible light Angew.Chem.,Int.Ed,2010,122(24):4190-4193. |
[6] | Abe R,Higashi M,Domen K.Facile fabrication of an efficient oxyniride TaON photoanode for overall water splitting into H2 and O2 under visible light irradiaiton.J.Am.Cherm.Soc.,2010,132(34):11828-11829. |
[7] | Maeda K,Teramura K,Lu D,et al.Photocatalyst releasing hydrogen from water.Nature,2006,440:295. |
[8] | Tian M K,Shangguan W F,Yuan J,et al.K4Ce2M10O30(M=Ta,Nb)as visible light-driven photocatalysts for hydrogen evolution from water decomposition.Applied Catalysis A:General,2006,309(1):76-83. |
[9] | Hochbaum A I,Yang P D.Semiconductor nanowires for energy conversion.Chem.Rev.,2010,110(1):527-546. |
[10] | Yoshino M,Kakihana M.Polymerizable complex synthesis of pure Sr2NbxTa2.xO7 solid solutions with high photocatalytic activities for water decomposition into H2 and O2.Chem.Mater.,2002,14(8):3369-3374. |
[11] | Brik F,Enjalbert R,Roucau C,et al.TTB structure of K4Ce2M10O30(M=Nb ro Ta):crystal growth and joint X-ray and hrem studies.J.Solid State Chem.1996,122(1):7-14. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%