以氨水为络合剂,NaOH为沉淀剂,通过共沉淀制备了高致密、粒度均匀的球形前驱体Ni0.8Co0.1Mn0.1(OH)2.通过焙烧该前驱体和LiOH·H2O的混合物制备出球形锂离子电池正极材料LiNi0.8Co0.1Mn0.1O2.采用XRD、SEM、TEM、TGA/DSC以及恒流充放电测试对材料的结构、形貌和电化学性能进行表征.结果表明,球形前驱体是由纳米级一次颗粒团聚形成,而不是晶粒的长大,且反应时间对前驱体的形貌、粒径分布及振实密度有显著影响.750℃焙烧16 h后的正极材料,保持了完好的球形形貌,具有最佳的层状结构和电化学性能,振实密度最大(2.98 g/cm3),首次放电容量为202.4 mAh/g,倍率性能佳,在3C的放电电流下容量为174.1 mAh/g,且循环性能优良,在40次循环以后,放电容量保持率为92.3％.
参考文献
| [1] | Kosova N V,Devyatkina E T.Comparative study of LiCoO2 surface modified with different oxide.J.Power Sources,2007,174(2):959-964. |
| [2] | Kim M H,Shin H S,Shin D,et al.Synthesis and electrochemical properties of LiNi0.8Co0.1Mn0.1O2 and LiNi0.8Co0.2O2 via co-precipitation.J.Power Sources,2006,159(2):1328-1333. |
| [3] | Yoon S H,Lee C W,Bae Y S,et al.Method of preparation for particle growth enhancement of LiNi0.8Co0.15Al0.05O2.Electrochemical and Solid-State Letters,2009,12(11):A211-A214. |
| [4] | Fergus J W.Recent developments in cathode materials for lithium ion batteries.J.Power Sources,2010,195(4):939-954. |
| [5] | 代克化,王银杰,冯华君,等(DAI Ke-Hua,et al).氢氧化物共沉淀法制备LiMn0.45Ni0.45Co0.1O2正极材料的反应条件.物理化学学报(Acta Phys-Chim.Sin.),2007,23(12):1927-1931. |
| [6] | Zhou F,Zhao X M,Bommel A V,et al.Coprecipitation synthesis of NixMn1-x(OH)2 mixed hydroxides.Chem.Mater.,2010,22(3):1015-1021. |
| [7] | Bommela A V,Dahn J R.Synthesis of spherical and dense particles of the pure hydroxide phase Ni1/3Mn1/3Co1/3(OH)2.J.Electrochemical Society,2009,156(5):A362-A365. |
| [8] | 王希敏,王先友,易四勇,等.层状锂离子电池正极材料LiNi0.8Co0.1Mn0.1O2的制备及性能.过程工程学报,2007,7(4):817-821. |
| [9] | Whitfield P S,Davidson I J,Cranswick L M D,et al.Investigation of possible superstructure and cation disorder in the lithium battery cathode materials LiNi1/3Mn1/3Co1/3O2 using neturon and anomalous dispersion powder diffraction.Solid State Ionics,2005,176(5/6):463-471. |
| [10] | Park S H,Shin H S,Myung S T,et al.Synthesis of nanostructured Li[Ni1/3Co1/3Mn1/3]O2 via a modified carbonate process.Chem.Mater.,2005,17(1):6-8. |
| [11] | LI Xin-Lu,KANG Fei-Yu,BAI Xin-De,et al.Microstructure and electrochemical properties of LiNi1/3Co1/3Mn1/3O2 coated with al2o3film.Journal of Inorganic Materials,2007,22(6):1037-1040. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%