为了深入理解草酸溶液中制备的阳极氧化铝(AAO)模板受热失重以及草酸根对模板发光性能的影响,利用程序升温脱附与质谱联用(TPD-MS)、热重分析(TGA)、差热分析(DTA)以及光致发光(PL)等技术对AAO模板进行了系统研究.热失重分析结果表明,当温度低于402.2℃时,发生H2O、CO以及CO2分子的脱附以及掺杂草酸的分解,其中H2O的脱附为失重的主要原因;在402.2~866.7℃范围内,主要是草酸盐分解放出CO和CO2引起失重,CO为主要产物;碳酸盐以及残余的草酸盐的剧烈分解发生在866.7~1022.9℃范围内,主要放出CO2,并且引起大量失重.由热重结果及脱附产物中CO的摩尔比得到草酸根残余量随处理温度的变化趋势.最后,对模板PL强度、草酸根含量以及氧空位缺陷(F+)浓度三者随处理温度的变化趋势进行了关联,对AAO模板发光的原因进行了分析.

参考文献

[1] Fan Z Y,Razavi H,Javey A,et al.Three-dimensional nanopillararray photovoltaics on low-cost and flexible substrates.Nat.Mater.,2009,8(8):648-653.
[2] Lee W,Han H,Lotnyk A,et al.Individually addressable epitaxial ferroelectric nanocapacitor arrays with near Tb inch-2 density.Nat.Nanotechnol.,2008,3(7):402-407.
[3] Borissov D,Isik-Uppenkamp S,Rohwerder M.Fabrication of iron nanowire arrays by electrodeposition into porous alumina.J.Phys.Chem.C,2009,113(8):3133-3138.
[4] Liu L H,Li H T,Sun H Y,et al.Fabrication and magnetic properties of Ni-Zn nanowire arrays.J.Magn.Magn.Mater.,2009,321(20):3511-3514.
[5] Xue F H,Fei G T,Wu B,et al.Direct electrodeposition of highly dense Bi/Sb superlattice nanowire arrays.J.Am.Chem.Soc.,2005,127(44):15348-15349.
[6] Zong R L,Zhou J,Li Q,et al.Synthesis and optical properties of silver nanowire arrays embedded in anodic alumina membrane.J.Phys.Chem.B,2004,108(43):16713-16716.
[7] Sun X Y,Xu F Q,Li Z M,et al.Cyclic voltammetry for the fabrication of high dense silver nanowire arrays with the assistance of AAO template.Mater.Chem.Phys.,2005,90(1):69-72.
[8] Chang M,Cao X L,Xu X J,et al.Fabrication and photoluminescence properties of highly ordered ZnS nanowire arrays embedded in anodic alumina membrane.Phys.Lett.A,2008,372(3):273-276.
[9] Ji H X,Hu J S,Wan L J,et al.Bis(ethylenedithio)tetrathiafulvalene charge-transfer salt nanotube arrays.Adv.Mater.,2006,18(20):2753-2757.
[10] Wu C,Shi J B,Chen C J,et al.Synthesis and optical properties of CuS nanowires fabricated by electrodeposition with anodic alumina membrane.Mater.Lett.,2008,62(6/7):1074-1077.
[11] 徐怡,徐金霞,将林华(XU Yi,et al).Co,Ni及其合金纳米线阵列的制备及磁性研究.无机化学学报(Chinese J.Inorg Chem.),2009,25(3):459-464.
[12] Shamaila S,Sharif R,Han X F,et al.Magnetic field annealing dependent magnetic properties of Co90Pt10 nanowire arrays.J.Magn.Magn.Mater.,2009,321(24):3984-3989.
[13] Ji H X,Guo Y G,Wan L J,et al.Ion-transfer-based growth:a mechanism for CuTCNQ nanowire formation.Adv.Mater.,2008,20(24):4879-4882.
[14] Liu X L,Xu F Q,Li Z M,et al.Synthesis and optical properties of poly[3-(2-methoxyphenyl)thiophene]nanowires confined in porous anodic alumina membrane.Opt.Mater.,2008,30(12):1861-1866.
[15] Yanagishita T,Nishio K,Masuda H,et al.Fabrication of monodisperse polymer nanoparticles by membrane emulsification using ordered anodic porous alumina. Langmuir, 2010, 26(3):1516-1519.
[16] Nee T E,Chen Y R,Fan P L,et al.Characterization of the anomalous luminescence properties from self-ordered porous anodic alumina with oxalic acid electrolytes.Thin Solid Films,2009,518(5):1439-1442.
[17] Wang J,Wang C W,Liu W M,et al.Optical constants of anodic aluminum oxide films formed in oxalic acid solution.Thin Solid Films,2008,516(21):7689-7694.
[18] TANG H J,WU F Q,WEI Y H,et al.Comparison of optical properties of Cu-Al2O3 and Ag-Al2O3 nano-array composite structure.Chin.Opt.Lett.,2005,3(12):722-724.
[19] Li Z J,Huang K L.Optical properties of alumina membranes prepared by anodic oxidation process.J.Lumin.,2007,127(2):435--440.
[20] Sun X Y,Xu F Q,Li Z M,et al.Photoluminescence properties of anodic alumina membranes with ordered nanopore arrays.J.Lumin.,2006,121(2):588-594.
[21] Du Y,Cai W L,Mo C M,et al.Preparation and photoluminescence of alumina membranes with ordered pore arrays.Appl.Phys.Lett.,1999,74(20):2951-2953.
[22] Huang G S,Wu X L,Mei Y F,et al.Strong blue emission from anodic alumina membranes with ordered nanopore array.J.Appl.Phys.,2003,93(1):582-585.
[23] Li Y,Li G H,Meng G W,et al.Photoluminescence and optical absorption caused by the F+ centres in anodic alumina membranes.J.Phys.:Condens.Matter,2001,13(11):2691-2699.
[24] Yamamoto Y,Baba N,Tajima S.Coloured materials and photoluminescence centres in anodic film on aluminium.Nature,1981,289(12):572-574.
[25] Gao T,Meng G W,Zhang L D.Blue luminescence in porous anodic alumina films:the role of the oxalic impurities.J.Phys.:Condens.Matter,2003,15(12):2071-2079.
[26] Fernández-Romero L,Montero-Moreno J M,Pellicer E,et al.Assessment of the thermal stability of anodic alumina membranes at high temperatures.Mater.Chem.Phys.,2008,111(2/3):542-547.
[27] Wang J A,Bokhimi X,Novaro O,et al.Aluminum local environment and defects in the crystalline structure of Sol-Gel alumina catalyst.J.Phys.Chem.B,1999,103(2):299-303.
[28] Xu W L,Zheng M J,Shen W Z,et al.Effects of high-temperature annealing on structural and optical properties of highly ordered porous alumina membranes.Appl.Phys.Lett.,2004,85(19):4364-4366.
[29] Wang X H,Li C Y,Cao H,et al.Preparation and thermal stability of porous alumina membranes with nano-pore arrays.Appl.Phys.A:Mater.Sci.Process.,2009,98(4):745-749.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%