采用化学沉淀法由HCl-Na2WO4制备WO3-C复合载体,通过微波辅助乙二醇还原法制备Pt/WO3-C复合载体催化剂.研究了WO3含量以及热处理温度对Pt/WO3-C催化剂性能的影响,采用X射线衍射、透射电子显微镜和能量散射光谱对Pt/WO3-C的物化结构和组成进行了表征.结果表明,WO3的最佳含量为10wt%,N2气氛中热处理适宜温度为250℃.所制备的Pt/WO3-C催化剂中WO3以单斜晶型存在,Pt颗粒的平均粒径为2.77 nm.通过循环伏安法和单体质子交换膜燃料电池极化曲线测试了Pt/WO3-C催化剂的电化学性能,证实了Pt与WO3之间存在协同催化作用,与Pt/C催化剂相比,Pt/WO3-C的催化活性和稳定性都有明显改善.
参考文献
[1] | Emadi A,Rajashekara K,Williamson S S,et al.Topological overview of hybrid electric and fuel cell vehicular power system architectures and configurations.IEEE T.Veh.Technol.,2005,54(3):763-770. |
[2] | Hwang J J,Wang D Y,Shih N C.Development of a lightweight fuel cell vehicle.J.Power Sources,2005,141(1):108-115. |
[3] | Yang S T,Cao Z X,Zhang Y F.Preparation and characteristic of new type nano rare earth electrocatalyst for PEMFC.J.Inorg.Mater.,2004,19(4):921-925. |
[4] | Xu Y,Tian J H,Luo W H,et al.Reprocessing of the ineffective Pt/C catalysts in PEMFC.Chin.J.Power Sources,2006,30(5):349-351. |
[5] | Shao Y Y,Liu J,Wang Y,et al.Novel catalyst support materials for PEM fuel cells:current status and future prospects.J.Mater.Chem.,2009,19(1):46-59. |
[6] | Shrestha S,Liu Y,Mustain W E.Electrocatalytic activity and stability of Pt clusters on state-of-the-art supports:a review.Cat.Rev.-Sci.Eng.,2011,53(3):256-336. |
[7] | Roen L M,Paik C H,Jarvic T D.Electrocatalytic corrosion of carbon support in PEMFC cathodes.Electrochem.Solid-State Lett.,2004,7(1):A19-A22. |
[8] | Chhina H,Campbell S,Kesler O.An oxidation-resistant indium tin oxide catalyst support for proton exchange membrane fuel cells.J.Power Sources,2006,161(2):893-900. |
[9] | Huang S Y,Ganesan P,Popov B N.Titania supported platinum catalyst with high electrocatalytic activity and stability for polymer electrolyte membrane fuel cell.Appl.Catal.,B-Environ.,2011,102(1/2):71-77. |
[10] | Liu X,Chen J,Liu G,et al.Enhanced long-term durability of proton exchange membrane fuel cell cathode by employing Pt/TiO2/C catalysts.J.Power Sources,2010,195(13SI):4098-4103. |
[11] | Sasaki K,Zhang L,Adzic R R.Niobium oxide-supported platinum ultra-low amount electrocatalysts for oxygen reduction.Phys.Chem.Chem.Phys.,2008,10(1):159-167. |
[12] | Ioroi T,Siroma Z,Fujiwara N,et al.Sub-stoichiometric titanium oxide-supported platinum electrocatalyst for polymer electrolyte fuel cells.Electrochem.Commun.,2005,7(2):183-188. |
[13] | Ioroi T,Senoh H,Yamazaki S,et al.Stability of corrosion-resistant Magnéli-phase Ti4O7-supported PEMFC catalysts at high potentials.J.Electrochem.Soc.,2008,155(4):B321-B326. |
[14] | Slavcheva E,Nikolova V,Petkova T,et al.Electrocatalytic activity of Pt and PtCo deposited on ebonex by BH reduction.Electrochim.Acta,2005,50(27):5444-5448. |
[15] | Chhina H,Campbell S,Kesler O.Ex situ evaluation of tungsten oxide as a catalyst support for PEMFCs.J.Electrochem.Soc.,2007,154(6):B533-B539. |
[16] | Ye J L,Liu J G,Zou Z G,et al.Preparation of Pt supported on WO3-C with enhanced catalytic activity by microwave-pyrolysis method.J.Power Sources,2010,195(9):2633-2637. |
[17] | Liu Y,Shrestha S,Mustain W E.Synthesis of nanosize tungsten oxide and its evaluation as an electrocatalyst support for oxygen reduction in acid media.ACS Catal.,2012,2(3):456-463. |
[18] | Kulesza P J,Faulkner L R.Electrocatalysis at a novel electrode coating of nonstoichiometric tungsten(Ⅵ,Ⅴ) oxide aggregates.J.Electrochem.Soc.,1988,110(15):4905-4913. |
[19] | Kulesza P J,Faulkner L R.Reactivity and charge transfer at the tungsten oxide/sulfuric acid interfaces:nonstoichiometric tungsten(Ⅵ,Ⅴ) oxide films as powerful electroreduction catalysts.Colloids Surf.,1989,41:123-134. |
[20] | Shim J,Lee C R,Lee H K,et al.Electrochemical characteristics of Pt-WO3/C and Pt-TiO2/C electrocatalysts in a polymer electrolyte fuel cell.J.Power Sources,2001,102(1/2):172-177. |
[21] | Zhang Z H,Wang X G,Cui Z M,et al.Pd nanoparticles supported on WO3-C hybrid material as catalyst for oxygen reduction reaction.J.Power Sources,2008,185(2):941-945. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%