制备了B位Fe取代的BaCo1-xFexO3-δ系列缺陷钙钛矿型NOx储存还原(NSR)催化剂,考察了其储存NOx与抗硫性能;应用N2吸附-脱附,X射线衍射,红外光谱,程序升温还原和程序升温脱附等技术对催化剂进行了表征.结果表明,Fe的取代提高了BaCoO3的抗硫能力,当x=0.4时,样品具有相对最大的NOx储存量,且在深度硫化条件下仍保持398μmol/g的NOx储存量,表现出很强的抗硫性能;催化剂性能与其表面晶格氧的活泼性及氧空位的数量密切相关,NOx在BaCo1-xFexO3-δ样品中的储存形式主要为离子态硝酸盐和单齿硝酸盐.
参考文献
[1] | Shelef M;Graham W G .[J].Catalysis Review:Science and Engineering,1994,36:433. |
[2] | Luo JY;Meng M;Zha YQ;Xie YN;Hu TD;Zhang J;Liu T .A comparative study of Pt/Ba/Al2O3 and Pt/Fe-Ba/Al2O3 NSR catalysts: New insights into the interaction of Pt-Ba and the function of Fe[J].Applied Catalysis, B. Environmental: An International Journal Devoted to Catalytic Science and Its Applications,2008(1/2):38-52. |
[3] | Milt V G;Querini C A;Miró E E;Ulla M A .[J].Journal of Catalysis,2003,220:424. |
[4] | Milt VG;Ulla MA;Miro EE .NOx trapping and soot combustion on BaCoO3-y perovskite: LRS and FTIR characterization[J].Applied Catalysis, B. Environmental: An International Journal Devoted to Catalytic Science and Its Applications,2005(1):13-21. |
[5] | 陈加福,孟明,林培琰,李新刚,伏义路,俞寿明.BaFeO3和BaCeO3钙钛矿型氧化物的储氮性能[J].催化学报,2003(06):419-422. |
[6] | Hodjati S;Petit C;Pitchon V;Kiennemann A .[J].Applied Catalysis B:Environmental,2001,30:247. |
[7] | 彭小圣,林赫,上官文峰,黄震.K和Cu部分取代对LaMnO3钙钛矿型催化剂同时去除Nox和碳烟的影响[J].催化学报,2006(09):767-771. |
[8] | Misono M .[J].Catalysis Today,2005,100:95. |
[9] | 朱琳琳,卢冠忠,王艳芹,郭耘,郭杨龙.制备方法对LaMn0.8Mg0.2O3钙钛矿型氧化物催化甲烷燃烧反应性能的影响[J].催化学报,2010(08):1006-1012. |
[10] | Li X G;Chen J F;Lin P Y;Meng M Fu Y L Tu J Li Q X .[J].Catalyst Communication,2004,5:25. |
[11] | Fanson P T;Horton M R;Delgass W N;Lauterbach J .[J].Applied Catalysis B:Environmental,2003,46:393. |
[12] | Liu Y;Meng M;Zou Z Q;Li X G Zha Y Q .[J].Catalyst Communication,2008,10:173. |
[13] | Zou Z Q;Meng M;Zhou X Y;Li X G Zha Y Q .[J].Catalysis Letters,2009,128:475. |
[14] | Roy, S;Baiker, A .NOx Storage-Reduction Catalysis: From Mechanism and Materials Properties to Storage-Reduction Performance[J].Chemical Reviews,2009(9):4054-4091. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%