采用同时共沉淀法制备了(CeO2-ZrO2-Al2O3)-(La2O3Al2O3)新型复合氧化物(CZA-LA),考察了焙烧温度对CZA-LA负载的Pd密偶催化剂的影响,并采用N2吸附-脱附法和X射线衍射对其进行了表征.结果表明,随着焙烧温度的升高,尽管CZA-LA样品的比表面积降低,但即使在1000℃焙烧5h后,其比表面积仍能保持在122 m2/g左右；另外,CZA-LA样品的孔体积降低幅度不大,当在700℃及更高温度下焙烧后基本上保持稳定.以不同温度焙烧5h后的样品为载体,采用等体积浸渍法制备了一系列整体式Pd/CZA-LA密偶催化剂(Pd含量2.0g/L).催化剂对消除模拟汽油车尾气中C3H8活性测试结果表明,各新鲜催化剂的活性相差不大,均具有较低的起燃温度Y50和完全转化温度T90.当催化剂经老化处理后,以1000℃焙烧的载体负载的Pd催化剂活性最高,T50和T90分别为310和341℃,ΔT仅为31℃,仅比新鲜催化剂的高7℃.可见,该催化剂表现出优异的催化活性和抗老化性能,可以满足欧Ⅳ及更高标准的用于汽油车尾气净化的密偶催化剂的性能要求.
参考文献
| [1] | Ka(s)par J;Fornasiero P;Hickey N .[J].Catalysis Today,2003,77:419. |
| [2] | Collins N R;Twigg M V .[J].Topics in Catalysis,2007,42-43:323. |
| [3] | Heck R M;Farrauto R J .[J].Applied Catalysis A:General,2001,221:443. |
| [4] | Martyn V T .[J].Catalysis Today,2006,117:407. |
| [5] | Martyn V T .[J].Applied Catalysis B:Environmental,2007,70:2. |
| [6] | Matsumoto S I .[J].Catalysis Today,2004,90:183. |
| [7] | Hu Z C;Heck R M;Rabinowitz H N .[P].US 6 044 644,2000. |
| [8] | Morikawa A;Suzuki T;Kanazawa T;Kikuta K Suda A Shinjo H .[J].Applied Catalysis B:Environmental,2007,78:210. |
| [9] | Sugiura M .[J].CatalSurvAsia,2003,7:77. |
| [10] | Rossignol S;Kappenstein C .[J].International Journal of Inorganic Materials,2001,3:51. |
| [11] | Stasinska B;Gac W;Ioannides T;Machocki A .[J].Journal of Natural Gas Chemistry,2007,16:342. |
| [12] | 刘勇,王敬先,杨竹仙,何阿弟,陈晓银.钡对氧化铝的高温热稳定作用[J].物理化学学报,2000(06):533. |
| [13] | Masakuni O .[J].Journal of Alloys and Compounds,2006,408-412:1090. |
| [14] | Church J S;Cant N W;Trimm D L .[J].Applied Catalysis A:General,1993,101:105. |
| [15] | 肖益鸿,李桂平,郑瑛,蔡国辉,魏可镁.ZrO_2-Al_2O_3复合氧化物的合成及其性能研究[J].无机化学学报,2010(01):61-66. |
| [16] | 史忠华,龚茂初,陈耀强.Pt-Rh密偶催化剂的制备及其催化控制汽车尾气排放的性能[J].催化学报,2006(08):647-649. |
| [17] | Nagai Y;Hirabayashi T;Dohmae K;Takagi N Minami T Shinjoh H Matsumoto S I .[J].Journal of Catalysis,2006,242:103. |
| [18] | Leofanti G;Padovan M;Tozzola G;Venturelli B .[J].Catalysis Today,1998,41:207. |
| [19] | Wang W;Lin P;FuY;Cao G .[J].Catalysis Letters,2002,82:19. |
| [20] | Long E Y;Zhang X Y;Li Y L;Liu Z M Wang Y Gong M C Chen Y Q .[J].Journal of Natural Gas Chemistry,2010,19:134. |
| [21] | Fernandes D M;Scofield C F;Neto A A;Cardoso M J B Zotin F M Z .[J].Chemical Engineering Journal,2010,160:85. |
| [22] | Zotin F M Z;Gomes O D M;de Oliveira C H;Alcover A A Cardoso M J B .[J].Catalysis Today,2005,107-108:157. |
| [23] | 姚艳玲,方瑞梅,史忠华,龚茂初,陈耀强.La2O3对Pd密偶催化剂性能的影响[J].催化学报,2011(04):589-594. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%