通过优化和组合不同脱铝补硅方法,依次经氟硅酸铵处理、600℃水热处理、硅溶胶+草酸处理和800℃水热处理过程,成功实现了200nm超细NaY分子筛的深度脱铝,最终产品骨架硅铝比高达27.3,比表面积为581.9m2/g,分子筛结晶度保持在65％以上.结果表明,对于超细NaY分子筛脱铝,第一步采用氟硅酸铵进行部分缺陷修补尤为重要根据分子筛晶粒尺寸不同,需严格控制氟硅酸铵用量和处理次数.当晶粒为200nm时,氟硅酸铵与分子筛骨架铝的摩尔比为0.16,处理一次较为适宜.在连续脱铝过程中及时补修脱铝产生的缺陷是保障超细NaY分子筛成功脱铝的关键,而采用氟硅酸铵、硅溶胶、800℃高温水热处理,可有效实施这种骨架修正作用.
参考文献
| [1] | Yin H L;Zhou T N;Liu Y Q;Chai Y M Liu C G .[J].Journal of Natural Gas Chemistry,2011,20:441. |
| [2] | Hu L Y;Zhang Z K;Xie S J;Liu S L Xu L Y .[J].Catalysis Communications,2009,10:900. |
| [3] | 尹海亮,周同娜,柳云骐,刘晨光.Y型分子筛纳米晶的制备及其在柴油加氢精制催化剂中的应用[J].石油炼制与化工,2011(07):43-47. |
| [4] | 刘克峰,胡林彦,刘盛林,谢素娟,徐龙伢.Y型分子筛的粒径对其催化乙烯和苯液相烷基化性能的影响[J].石油学报（石油加工）,2009(z2):1-4. |
| [5] | Faghihian H;Godazandeha N .[J].Journal of Porous Materials,2009,16:331. |
| [6] | 胡林彦,谢素娟,王清遐,刘盛林,徐龙伢.无导向剂直接水热合成小粒径的NaY分子筛[J].催化学报,2007(09):761-765. |
| [7] | Song W;Grassian V H;Larsen S C.[J].Chemical Communications,2005:2951. |
| [8] | Holmberg B A;Wang H T;Norbeck J M;Yan Y S .[J].Microporous and Mesoporous Materials,2003,59:13. |
| [9] | 桑石云,田鹏,孟霜鹤,张阳阳,刘子玉,刘中民.小晶粒Y分子筛的合成及其晶化过程研究[J].石油化工,2005(z1):371-373. |
| [10] | Holmberg B A;Wang H T;Yan Y H .[J].Microporous and Mesoporous Materials,2004,74:189. |
| [11] | 马跃龙;陈诵英;彭少逸 .[J].催化学报,1995,16:410. |
| [12] | 刘欣梅,梁海宁,李亮,杨婷婷,阎子峰.以催化裂化废催化剂粉合成超细Y型分子筛[J].催化学报,2010(07):833-838. |
| [13] | Pal-Borbely G.;Beyer HK. .Isomorphous solid-state substitution of Si for framework Al in Y zeolite using crystalline (NH4)(2)[SiF6] as reactant[J].Physical chemistry chemical physics: PCCP,2003(10):2145-2153. |
| [14] | 谢鹏;张盈珍;郑禄彬 .[J].催化学报,1993,14:300. |
| [15] | Pal-Borbely G.;Beyer HK. .Repeatedly performed solid-state substitution of silicon for framework aluminium in Y zeolite using crystalline (NH4)(2)[SiF6] as dealumination agent[J].Physical chemistry chemical physics: PCCP,2003(24):5544-5551. |
| [16] | Pires J;Carvalho A;Pinto M;Rocha J .[J].Journal of Porous Materials,2006,13:107. |
| [17] | Salman, N;Ruscher, CH;Buhl, JC;Lutz, W;Toufar, H;Stocker, M .Effect of temperature and time in the hydrothermal treatment of HY zeolite[J].Microporous and Mesoporous Materials,2006(1/3):339-346. |
| [18] | Lutz W;Ruscher C H;Heidemann D .[J].Microporous and Mesoporous Materials,2002,55:193. |
| [19] | 刘兴云;张旭政;李宣文 .[J].高等学校化学学报,1999,18:342. |
| [20] | Najar H;Zina M S;Ghorbel A .[J].Reac Kinet Mech Catal,2010,100:385. |
| [21] | 罗一斌;胡颖;舒兴田;何鸣元 .[P].CN 1 205 981,1999. |
| [22] | Engelhardt G;Michel D.High Resolution Solid State NMR of Silicates and Zeolites[M].New York:John Wiley and Sons,Inc,1987:211. |
| [23] | Gore K U;Abraham A;Hegde S G;Kumar R Amoureux J P Ganapathy S .[J].Journal of Physical Chemistry B,2002,106:6115. |
| [24] | Datka J.;Gil B.;Baran P. .IR study of heterogeneity of OH groups in zeolite HY-splitting of OH and OD bands[J].Journal of Molecular Structure,2003(1):45-49. |
| [25] | 牛国兴;朱祟业;李全芝;薛志元 赵琰 侯运铎 李明时 .[J].物理化学学报,1993,9:374. |
| [26] | Matharu A P;Gladden L F;Carr S W .[J].Stud SurfSci Catal,1995,94:147. |
| [27] | Lohse U;Mildebrath M .[J].ZAnorgan Allg Chem,1981,476:126. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%