以聚乙二醇和共嵌段化合物F127为双模板剂,采用溶胶-凝胶辅助水热法制备了球形介孔TiO2 (MS-TiO2).采用扫描电镜、透射电镜、X射线衍射、热重分析和低温N2吸附-脱附对样品进行了结构表征,并以苯酚为降解模型物在紫外光下对其活性进行了评价.结果表明,所得TiO2为球形介孔结构,孔径为6.5～12.6 nm,比表面积最高可达106.9 m2/g,孔体积0.21 cm3/g,球形颗粒直径200～300 nm,由粒径为15～20 nm的小晶粒组成.随着焙烧温度的升高,TiO2的比表面积和孔体积减小,孔径增大.双模板剂的使用比单一模板剂更能形成稳定的立体网状球形胶束,并有效抑制TiO2前驱体的团聚,诱导其形成球形介孔结构.其中,在500℃下焙烧所制MS-TiO2样品表现最高的光催化活性,苯酚降解率达86.4％,为TiO2的1.3倍.
参考文献
| [1] | Yang H X;Qian J F;Chen Zh X;Ai X P Cao Y L .[J].Journal of Physical Chemistry C,2007,111:14067. |
| [2] | 唐玉朝,黄显怀,俞汉青,胡春.非金属掺杂改性TiO2光催化剂的机理[J].化学进展,2007(02):225-233. |
| [3] | He Z L;Zhu Zh F;Li J Q;Zhou J Q Wei N .[J].Journal of Hazardous Materials,2011,190:133. |
| [4] | 王晓静,刘超,胡中华,刘亚菲,陈玉娟,温祖标.多孔二氧化钛微球的制备、表征及其光催化性能[J].催化学报,2008(04):391-396. |
| [5] | Varghese, OK;Paulose, M;Grimes, CA .Long vertically aligned titania nanotubes on transparent conducting oxide for highly efficient solar cells[J].Nature nanotechnology,2009(9):592-597. |
| [6] | Choi S Y;Mamak M;Coombs N;Chopra N OzinG A .[J].Advanced Functional Materials,2004,14:335. |
| [7] | Dong A G;Ren N;Tang Y;Wang Y J Zhang Y H Hua W M Gao Z .[J].Journal of the American Chemical Society,2003,125:4976. |
| [8] | 向全军,余家国.暴露{001}面TiO2纳米片分等级花状结构的制备及其光催化活性[J].催化学报,2011(04):525-531. |
| [9] | 丁玉兰,柏扬,李伟,陈闪山,朱育丹,朱银华,杨祝红,陆小华.Pt改性的高结晶度TiO2晶须的光催化性能[J].催化学报,2010(10):1271-1276. |
| [10] | Serrano D P;Calleja G;Sanz R;Pizarro P.[J].Chemical Communications,2004:1000. |
| [11] | Peng T Y;Zhao D;Dai K;Shi W Hirao K .[J].Journal of Physical Chemistry B,2005,109:4947. |
| [12] | Yu J C;Yu J G;Zhang L Zh;Ho W .[J].Journal of Photochemistry and Photobiology A:Chemistry,2002,148:263. |
| [13] | Zhang Sh Q;Wen W;Jiang D L;Zhao H J John R Wilson G J Will G D .[J].Journal of Photochemistry and Photobiology A:Chemistry,2006,179:305. |
| [14] | Yoshitake H.;Sugihara T.;Tatsumi T. .Preparation of wormhole-like mesoporous TiO2 with an extremely large surface area and stabilization of its surface by chemical vapor deposition[J].Chemistry of Materials,2002(3):1023-1029. |
| [15] | 李伟,赵莹,刘守新.以纳米微晶纤维素为模板的酸催化水解法制备球形介孔TiO2[J].催化学报,2012(02):342-347. |
| [16] | Jing X Zh;Li Y X;Yang Q B;Yin Q R .[J].Materials Science and Engineering B,2004,110:18. |
| [17] | Antonelli D M;Ying J Y .[J].Angew Chem Int Ed Int Ed,1995,34:2014. |
| [18] | Yang P D;Zhao D Y;Margolese D I;Chmelka B F Stucky G D .[J].Nature,1998,396:152. |
| [19] | Yusuf M M;Imai H;Hirashima H .[J].Journal of Sol-Gel Science and Technology,2003,28:97. |
| [20] | 王晓静,刘超,胡中华,刘亚菲,陈玉娟,温祖标.多孔二氧化钛微球的制备、表征及其光催化性能[J].催化学报,2008(04):391-396. |
| [21] | Chen D H;Huang F Zh;Cheng Y B;Caruso R A .[J].Advanced Materials,2009,21:2206. |
| [22] | Sheng, QR;Cong, Y;Yuan, S;Zhang, JL;Anpo, M .Synthesis of bi-porous TiO2 with crystalline framework using a double surfactant system[J].Microporous and Mesoporous Materials,2006(1/3):220-225. |
| [23] | Smatt JH.;Schunk S.;Linden M. .Versatile double-templating synthesis route to silica monoliths exhibiting a multimodal hierarchical porosity[J].Chemistry of Materials,2003(12):2354-2361. |
| [24] | Zhao J Q;Wan P;Xiang J;Tong T Dong L Gao Zh N Shen X Y Tong H .[J].Microporous and Mesoporous Materials,2011,138:200. |
| [25] | Zhang X T;Zhou G W;Xu J;Bai G W Wang L .[J].Journal of Solid State Chemistry,2010,183:1394. |
| [26] | Kim D S;Ham S J;Kwak S Y .[J].Journal of Colloid and Interface Science,2007,316:85. |
| [27] | 刘守新,陈孝云,陈曦.酸催化水解法制备可见光响应N掺杂纳米TiO2催化剂[J].催化学报,2006(08):697-702. |
| [28] | Hüsing N;Launay B;Doshi D;Kickelbick G .[J].Chemistry of Materials,2002,14:2429. |
| [29] | Torma V;Peterlik H;Bauer U;Rupp W Hüsing N Bernstorff S Steinhart M Goerigk G Schubert U .[J].Chemistry of Materials,2005,17:3146. |
| [30] | Shrinivasan S;Breadmore MC;Hosticka B;Landers JP;Norris PM .Toward optimization of macroporous silica gels for application to capillary or microchip-based CEC and LC[J].Journal of Non-Crystalline Solids: A Journal Devoted to Oxide, Halide, Chalcogenide and Metallic Glasses, Amorphous Semiconductors, Non-Crystalline Films, Glass-Ceramics and Glassy Composites,2004(0):391-396. |
| [31] | 刘茜,李宏旭,钱斌,高焕新,王仰东,唐颐,谢在库.双模板法制备介孔/大孔复合孔结构硅胶独石[J].催化学报,2008(08):733-740. |
| [32] | 张雅心,张学军.模板剂对介孔碳孔道结构及有序性的影响[J].北京化工大学学报（自然科学版）,2010(05):83-87. |
| [33] | Yang J;Ferreira J M F .[J].Materials Letters,1998,36:320. |
| [34] | Yu JG;Wang GH;Cheng B;Zhou MH .Effects of hydrothermal temperature and time on the photocatalytic activity and microstructures of bimodal mesoporous TiO2 powders[J].Applied Catalysis, B. Environmental: An International Journal Devoted to Catalytic Science and Its Applications,2007(3/4):171-180. |
| [35] | Parida, K.M.;Naik, B. .Synthesis of mesoporous TiO_(2 - x)N_x spheres by template free homogeneous co-precipitation method and their photo-catalytic activity under visible light illumination[J].Journal of Colloid and Interface Science,2009(1):269-276. |
| [36] | Guo W;Luo G S;Wang Y J .[J].Journal of Colloid and Interface Science,2004,271:400. |
| [37] | Alberius PCA.;Frindell KL.;Hayward RC.;Kramer EJ.;Stucky GD.;Chmelka BF. .General predictive syntheses of cubic, hexagonal, and lamellar silica and titania mesostructured thin films[J].Chemistry of Materials,2002(8):3284-3294. |
| [38] | Yoo, KS;Lee, TG;Kim, J .Preparation and characterization of mesoporous TiO2 particles by modified sol-gel method using ionic liquids[J].Microporous and Mesoporous Materials,2005(1/3):211-217. |
| [39] | Shamaila S;Sajjad A K L;Chen F;Zhang J L .[J].Catalysis Today,2011,175:568. |
| [40] | Bu Sh J;Jin Zh G;Liu X X;Yang L R Cheng Zh J .[J].Materials Chemistry and Physics,2004,88:273. |
| [41] | Yu J C;Zhang L Zh;Yu J G .[J].New Journal of Chemistry,2002,26:416. |
| [42] | Ding XJ;An TC;Li GY;Zhang SQ;Chen JX;Yuan JM;Zhao HJ;Chen H;Sheng GY;Fu JM .Preparation and characterization of hydrophobic TiO2 pillared clay: The effect of acid hydrolysis catalyst and doped Pt amount on photocatalytic activity[J].Journal of Colloid and Interface Science,2008(2):501-507. |
| [43] | Blin J L;Leonard A;Yuan Zh Y;Gigot L,Vantomme A,Cheetham A K,Su B L .[J].Angewandte Chemie International Edition,2003,42:2872. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%