采用水热法可控合成了花状TiO2分级结构材料,运用扫描电镜、透射电镜、X射线衍射、N2物理吸附-脱附等手段,对其进行了表征,系统研究了NaOH用量、H2O2浓度、HNO3浓度、反应温度及时间等因素对所得样品形貌的影响,并评价了它们的光催化性能.结果表明,花状TiO2分级结构为锐钛矿相,颗粒大小均一;随制备条件的变化,构成花状TiO2分级结构的基元结构分别为纳米线、纳米片,纳米线直径约25 nm,纳米片厚度不足10 nm;该样品具有较高的比表面积,表现出良好的单次光催化活性与重复使用性能.
参考文献
[1] | Tryk D A;Fujishima A;Honda K .[J].Electrochimica Acta,2000,45:2363. |
[2] | Vidal F J G;Moreno E .[J].NATURE,2009,461:604. |
[3] | 李纲,刘中清,张昭,颜欣.水热法制备TiO2纳米管阵列[J].催化学报,2009(01):37-42. |
[4] | 王后锦,吴晓婧,王亚玲,焦自斌,颜声威,黄浪欢.二氧化钛纳米管阵列光电催化同时降解苯酚和Cr(VI)[J].催化学报,2011(04):637-642. |
[5] | Chen, W.;Fan, Z.;Zhang, B.;Ma, G.;Takanabe, K.;Zhang, X.;Lai, Z. .Enhanced visible-light activity of titania via confinement inside carbon nanotubes[J].Journal of the American Chemical Society,2011(38):14896-14899. |
[6] | Ni Y H;Zhu Y;Ma X .[J].DALTON TRANSACTIONS,2011,40:3689. |
[7] | Zhang J;Xu Q;Feng Zh Ch;Li M J,Li C .[J].Angew Chem IntEd,2008,47:1766. |
[8] | Kuang D B;Uchida S;Humphry-Baker R;Zakeeruddin S M,Gr(a)tzel M .[J].Angew Chem Int Ed,2008,47:1923. |
[9] | 肖尧明,吴季怀,岳根田,林建明,黄妙良,范乐庆,兰章.单晶二氧化钛纳米线的制备及其在柔性染料敏化太阳能电池中的应用[J].物理化学学报,2012(03):578-584. |
[10] | Buso D;Post M;Cantalini C;Mulvaney P Martucci A .[J].Adv FunctMater,2008,18:3843. |
[11] | Chen X B;Shen Sh H;Guo L J;Mao S S .[J].CHEMICAL REVIEWS,2010,110:6503. |
[12] | Xue B;Liu R;Xu Zh D .[J].Materials Letters,2009,63:2377. |
[13] | Zhou T F;Hu J Ch .[J].Environmental Science and Technology,2010,44:8698. |
[14] | SunQ;XuYM .[J].JPhysChemC,2010,114:18911. |
[15] | Liu Y;Chen L F;Hu J Ch;Li J L Richards R .[J].J Phys Chem C,2010,114:1641. |
[16] | Liu M N;Yan Ch;Bell J;Will G .[J].Nanosci Nanotechnol Lett,2011,3:407. |
[17] | Wu N Q;Wang J;Tafen D N;Wang H Zheng J G Lewis J P Liu X G Leonard S S Manivannan A .[J].Journal of the American Chemical Society,2010,132:6679. |
[18] | Liu, B;Aydil, ES .Growth of Oriented Single-Crystalline Rutile TiO2 Nanorods on Transparent Conducting Substrates for Dye-Sensitized Solar Cells[J].Journal of the American Chemical Society,2009(11):3985-3990. |
[19] | Zorba V;Chen X B;Mao S S .[J].Applied Physics Letters,2010,96:93702. |
[20] | Song C X;Wang D B;Xu Y H;Hu Zh Sh .[J].Materials Letters,2011,65:908. |
[21] | Yun J;Jin D;Lee Y S;Kim H I .[J].Materials Letters,2010,64:2431. |
[22] | Hochbaum A I;Yang P P .[J].CHEMICAL REVIEWS,2010,110:527. |
[23] | Liu, G.;Yu, J.C.;Lu, G.Q.;Cheng, H.-M. .Crystal facet engineering of semiconductor photocatalysts: Motivations, advances and unique properties[J].Chemical communications,2011(24):6763-6783. |
[24] | Zhang H J;Wu R F;Chen Zh W;Liu G Zhang Z N Jiao Zh .[J].Cryst Eng Commun,2012,14:1775. |
[25] | Ko Y H;Leem J W;Yu J S .[J].NANOTECHNOLOGY,2011,22:205604. |
[26] | Li J;Fan H Q;Jia X H .[J].JPhys Chem C,2010,114:14684. |
[27] | Xiang G L;Li T Y;Zhuang J;Wang X.[J].Chemistry Communications,2010:6801. |
[28] | Sun Z Q;Kim J H;Zhao Y;Bijarbooneh F Malgras V Lee Y KangY M Dou S X .[J].Journal of the American Chemical Society,2011,133:19314. |
[29] | 相国磊,王训.纳米晶核的尺寸与表面对生长与组装过程影响的研究进展[J].无机化学学报,2011(12):2323-2331. |
[30] | Penn R L;Banfield J F .[J].SCIENCE,1998,281:969. |
[31] | Banfield J F;Welch S A;Zhang;H Z Ebert T T Penn R L .[J].SCIENCE,2000,289:751. |
[32] | Xiang G L;Wu D;He J;Wang X .[J].Chemistry Communications,2011,47:11456. |
[33] | Tao F F;Shen Y M;Wang L X .[J].MOLECULES,2012,17:703. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%