利用溶胶-凝胶技术,以尿素为氮源,采用原位掺杂方式制备了TiO2-yNx纳米粉体;以亚甲基蓝(MB)溶液在可见光下的光催化降解评价其可见光催化活性;考察了体系初始pH值、N的掺杂量和焙烧温度对样品可见光催化活性的影响. 结合XRD、XPS、ESR和DRS测试技术,研究了N掺杂纳米TiO2的可见光响应机理. 研究结果表明,TiO2-yNx纳米粉体的优化制备工艺条件为:体系初始pH=0.52,掺杂比n(N): n(Ti)=1: 6,焙烧温度为440 ℃. 此条件下制备的样品N含量为0.77%,为单一的锐钛矿相,平均粒径为19.0 nm,具有良好的可见光催化活性. N掺杂导致TiO2纳米粉体的表面羟基含量增加,形成了大量束缚单电子的氧空位;N取代晶格O形成了N-Ti-O和O-N-Ti键合结构. N掺杂导致TiO2纳米粒子的吸收带边红移,对可见光的吸收能力明显增强,这表明N掺杂改变TiO2电子结构,使带隙窄化,降低光响应阈值. N掺杂TiO2纳米粒子的可见光响应归因于N取代掺杂形成的掺杂能级与氧空位形成的缺陷能级共同作用所致.
参考文献
| [1] | Zhao X J,Zhao Q N,Yu J G,Liu B S.J Non-Crystal Solids[J],2008,354:1424 |
| [2] | JIANG Hong-Quan(姜洪泉),WANG Peng(王鹏),XIAN Heng-Ze(线恒泽).Acta Chim Sin(化学学报)[J],2006,64(2):145 |
| [3] | SHI Jian-Wen(石建稳),CHEN Shao-Hua(陈少华),WANG Shu-Mei(王淑梅),LUO Hong-Yuan(罗红元).Chem Ind Eng Prog(China)(化工进展)[J],2009,28(2):251 |
| [4] | Sato S.Chem Phys Lett[J],1986,123(122):126 |
| [5] | Asahi R,Morikawa T,Ohwaki T,Aoki K,Taga Y.Science[J],2001,293:269 |
| [6] | Irie H,Watanabe Y,Hashimoto K.J Phys Chem B[J],2003,107(23):5483 |
| [7] | Ihara T,Miyoshi M,Iriyama Y,Marsumato O,Sugihara S.Appl Catal B:Environ[J],2003,42(4):403 |
| [8] | Sato S,Nakamura R,Abe S.Appl Catal A:General[J],2005,284:131 |
| [9] | Peng F,Cai L F,Huang L,Yu H,Wang H J.J Phys Chem Solids[J],2008,69:1657 |
| [10] | Pomoni K,Vomvas A,Trapalis C.J Non-Crystal Solids[J],2008,354:4448 |
| [11] | Xing M Y,Zhang J L,Chen F.Appl Catal B:Environ[J],2009,89:563 |
| [12] | FENG Guang-Jian(冯光建),LIU Su-Wen(刘素文),XIU Zhi-Liang(修志亮),YU Jiao-Xian(俞娇仙),LUO Jie(罗杰).J Chinese Rare Earth[J],2008,26(2):148 |
| [13] | REN Ling(任凌),YANG Fa-Da(杨发达),ZHANG Yuan-Ming(张渊明),YANG Jun(杨骏),LI Ming-Yu(李明玉).Chinese J Inorg Chem(无机化学学报)[J],2008,24(4):541 |
| [14] | Liu B S,Wen L P,Zhao X J.Sol Energy Mater Sol Cells[J],2008,92:1 |
| [15] | Nakano Y,Morikawa T,Ohwaki T,Taga Y.Chem Phys[J],2007,339:20 |
| [16] | Li Y Z,Hwang D S,Lee N H,Kim S J.Chem Phys Lett[J],2005,404:25 |
| [17] | Chen Q L,Tang C Q,Zheng G.Phys B:Conden Matter[J],2009,404:1074 |
| [18] | Sathish M,Viswanathan B,Viswanath R P,Gopinath C S.Chem Mater[J],2005,17(25):6349 |
| [19] | Rengifo-Herrera J A,Mielczarski E,Mielczarski J,Castillo N C,Kiwi J,Pulgarin C.Appl Catal B:Environ[J],2008,84:448 |
| [20] | Sun H Q,Bai Y,Cheng Y P,Jin W Q,Xu N P.Ind Eng Chem Res[J],2006,45:4971 |
| [21] | Chen X F,Wang X C,Hou Y D,Huang J H,Wu L,Fu X Z.J Catal[J],2008,255:59 |
| [22] | JING Li-Qiang(井立强),SUN Xiao-Jun(孙晓君),CAI Wei-Min(蔡伟民),LI Xiao-Qian(李晓倩),FU Hong-Gang(付宏刚),HOU Hai-Ge(候海鸽),FAN Nai-Ying(范乃英).Acta Chim Sin(化学学报)[J],2003,61(8):1241 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%