以多端羟基聚酯为引发剂,经丙交酯开环聚合得到多臂聚乳酸(MA-PLA). MA-PLA在DSC二次升温过程中,出现明显的冷结晶峰(41.5 J/g)和熔融峰(42.5 J/g),而工业产品聚乳酸PLLA 3051D没有这2个峰,确认该多臂聚乳酸的结晶能力优于3051D. MA-PLA多臂聚乳酸的左旋乳酸单元含量为97%,高于3051D的91%. 将MA-PLA与PLLA 3051D共混后,在DSC二次升温过程中出现了熔融峰和冷结晶峰. 偏光显微镜观察表明,共混物的成核速率和初期球晶生长速度加快. 等温结晶动力学数据表明,110 ℃等温结晶的半结晶时间由空白样品的53.6 min缩短至共混物的31.7 min,Avrami指数n由空白样品的2.25增加至共混物的2.60,可见多臂聚乳酸对线形聚乳酸结晶性能的改善,主要是加快了成核速率.
参考文献
| [1] | Kikkawa Y,Abe H,Iwata T,Doi Y.Biomacromolecules[J],2001,2:940 |
| [2] | Urayama H,Kananmori T,Fukushima K,Kimura Y.Polymer[J],2003,44:5635 |
| [3] | Koyama N,Doi Y.Polymer[J],1997,38:1589 |
| [4] | Park J W,Im S S.J Appl Polym Sci[J],2002,86:647 |
| [5] | Choi N S,Kim C H,Cho K Y,Park J K.J Appl Polym Sci[J],2002,86:1892 |
| [6] | Shibata M,Inoue Y,Miyoshi M.Polymer[J],2006,47:3557 |
| [7] | Lin Y,Zhang K Y,Dong Z M,Dong L S,Li Y S.Macromolecules[J],2007,40:6257 |
| [8] | Hu X,An H N,Li Z M,Geng Y,Li L B,Yang C L.Macromolecules[J],2009,42:3215 |
| [9] | Liu A X,Hong Z K,Zhuang X L,Chen X S,Cui Y,Liu Y,Jing X B.Acta Biomater[J],2008,4:1005 |
| [10] | Zhao Y L,Shuai X T,Chen C F,Xi F.Chem Mater[J],2003,15:2836 |
| [11] | Zuideveld M,Gottschalk C,Kropfinger H,Thomann R,Rusu M,Frey H.Polymer[J],2006,47:3740 |
| [12] | Malmstr(o)m E,Johansson M,Hult A.Macromolecules[J],1995,28:1698 |
| [13] | Thakur K A M,Kean R T,Hall E S,Kolstad J J,Lindgren T A.Macromolecules[J],1997,30:2422 |
| [14] | He P H,Wu Y,Wu R F.Curr Appl Phys[J],2007,7:63 |
| [15] | Thakur K A M,Kean R T,Hall E S,Doscotch M A,Munson E J.Anal Chem[J],1997,69:4303 |
| [16] | Thakur K A M,Kean R T,Hall E S,Kolstad J J,Munson E J.Macromolecules[J],1998,31:1487 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%