研究了界面具有化学键接的茂金属聚乙烯/聚合型改性蒙脱土(mPE/P-MMT)纳米复合材料的流变学行为. 结果表明,与均聚聚乙烯及非界面键接的茂金属聚乙烯/十二铵改性蒙脱土(mPE/12-MMT)复合材料相比,mPE/P-MMT纳米复合材料具备由聚乙烯基体与P-MMT所组成的网络结构,因此具有较高的熔体强度(在190 ℃时的熔体强度为12.0 cN). 用超临界二氧化碳作发泡剂对它们的发泡性能进行对比,mPE/P-MMT纳米复合材料具有更高的发泡倍率(可达14.7),其最佳发泡温度为142 ℃.
参考文献
| [1] | Han X,Koelling K W,Tomasko D L.Polym Eng Sci[J],2002,42:2094 |
| [2] | Xu X,Park C B,Xu D.Polym Eng Sci[J],2003,43:1378 |
| [3] | Kendall J L,Canelas D A,Young J L,DeSimone J M.Chem Rev[J],1999,99:543 |
| [4] | Liu J,Han B,Li G,Liu Z,He J,Yang G.Fluid Phase Equilib[J],2001,187:247 |
| [5] | Nalawade S P,Picchioni F,Janssen L P B M.Prog Polym Sci[J],2006,31:19 |
| [6] | Cooper A I.Adv Mater[J],2003,15:1049 |
| [7] | Klempner D,Frisch K C.Handbook of Polymeric Foams and Foam Technology[M].Munich,Vienna:Hanser Publishers,1991 |
| [8] | Ren C Y,Jiang Z Y,Du X H,Men,Y F,Tang T.J Phys Chem B[J],2009,113:14118 |
| [9] | Kharchenko S B,Douglas J F,Obrzut J,Grulke E A,Milger K B.Nat Mater[J],2004,3:564 |
| [10] | Okamoto M,Nam P H,Maiti P,Kotaka T,Nakayama T,Takada M,Ohshima M,Usuki A,Hasegawa N,Okamoto H.Nano Lett[J],2001,1:503 |
| [11] | Zhang P,Zhou N Q,Wu Q F,Wang M Y,Peng X F.J Appl Polym Sci[J],2007,104:4149 |
| [12] | Manninen A,Naguib H E,Nawaby A V,Xia L,Day M.Cell Polym[J] 2005,24:49 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%