将有机磷酸(乙二醇单甲醚磷酸酯和乙二醇单甲醚磷酸二酯混合物)(0P)掺杂得到的导电聚苯胺(PANI-OP)加入到水性环氧树脂(WER)中,制备了聚苯胺水性防腐涂料,并且研究了其防腐蚀性能和防腐蚀机理.透射电子显微镜观察表明,导电聚苯胺质量分数为0.1％时,其粒径分布范围为50 ～ 100 nm.电化学阻抗谱以及开路电压的变化表明,聚苯胺的存在显著提高了涂层的防腐效果.金属基底光电子能谱结果表明,聚苯胺水性涂料良好的防腐性能缘于在金属表面生成了致密的氧化物膜以及掺杂剂离子与溶解金属生成了不溶性的盐.
参考文献
| [1] | Deberry D W.Modification of the Electrochemical and Corrosion Behavior of Stainless Steels with an Electroactive Coating[J].J Electrochem Soc,1985,132(5):1022-1026. |
| [2] | Talo A,Forsen O,Ylasaari S.Corrosion Protective Polyaniline Epoxy Blend Coatings on Mild Steel[J].Synth Met,1999,102 (1/3):1394-1395. |
| [3] | Goncalves G S,Baldissera A F,Rodrigues Jr L F,et al.Alkyd Coatings Containing Polyanilines for Corrosion Protection of Mild Steel[J].Synth Met,2011,161(3/4):313-323. |
| [4] | Lu J L,Liu N J,Wang X H,et al.Mechanism and Life Study on Polyaniline Anti-corrosion Coating[J].Synth Met,2003,135/136:237-238. |
| [5] | Dominis A J,Spinks G M,Wallace G G.Comparison of Polyaniline Primers Prepared with Different Dopants for Corrosion Protection of Steel[J].Prog Org Coat,2003,48(1):43-49. |
| [6] | Kamaraj K,Sathiyanarayanan S,Muthukrishnan S,et al.Corrosion Protection of Iron by Benzoate Doped Polyaniline Containing Coatings[J].Prog Org Coat,2009,64 (4):460-465. |
| [7] | Pud A A,Shapoval G S,Kamarchik P,et al.Electrochemical Behavior of Mild Steel Coated by Polyaniline Doped with Organic Sulfonic Acids[J].Synth Met,1999,107(2):111-115. |
| [8] | Syed Azim S,Sathiyanarayanan S,Venkatachari G.Anticorrosive Properties of PANI-ATMP Polymer Containing Organic Coating[J].Prog Org Coat,2006,56(2/3):154-158. |
| [9] | Wessling B.Passivation of Metals by Coating with Polyaniline-Corrosion Potential Shift and Morphological-Changes[J].Adv Mater,1994,6(3):226-228. |
| [10] | Epstein A J,Smallfield J A O,Guan H,et al.Corrosion Protection of Aluminum and Aluminum Alloys by Polyanilines:A Potentiodynamic and Photoelectron Spectroscopy Study[J].Synth Met,1999,102(1/3):1374-1376. |
| [11] | Torresi R M,Souza Sd,Silva J E Pd,et al.Galvanic Coupling Between Metal Substrate and Polyaniline Acrylic Blends:Corrosion Protection Mechanism[J].Electrochim Acta,2005,50 (11):2213-2218. |
| [12] | Williams G,Gabriel A,Cook A,et al.Dopant Anion Effects in the Inhibition by Polyaniline of Corrosion-Driven Organic Coating Delamination on Iron[J].J Electrochem Soc,2006,153(10):B425-B433. |
| [13] | da Silva J E P,de Torresi S I C,Torresi R M.Polyaniline/poly(methylmethacrylate) Blends for Corrosion Protection:The Effect of Passivating Dopants on Different Metals[J].Prog Org Coat,2007,58(1):33-39. |
| [14] | Kinlen P J,Menon V,Ding Y W. A Mechanistic Investigation of Polyaniline Corrosion Protection Using the Scanning Reference Electrode Technique[J].J Electrochem Soc,1999,146(10):3690-3695. |
| [15] | Schauer T,Joos A,Dulog L,et al.Protection of Iron Against Corrosion with Polyaniline Primers[J].Prog Org Coat,1998,33(1):20-27. |
| [16] | Wessling B. Dispersion as the Link Between Basic Research and Commercial Applications of Conductive Polymers (polyaniline)[J].Synth Met,1998,93 (2):143-154. |
| [17] | Zubielewicz M,Gnot W.Mechanisms of Non-toxic Anticorrosive Pigments in Organic Waterborne Coatings[J].Prog Org Coat,2004,49(4):358-371. |
| [18] | Park J H,Lee G D,Nishikata A,et al.Anticorrosive Behavior of Hydroxyapatite as an Environmentally Friendly Pigment[J].Corros Sci,2002,44(5):1087-1095. |
| [19] | Shi A,Koka S,Ullett J.Performance Evaluation on the Weathering Resistance of Two USAF Coating Systems(standard 85285 topcoat versus fluorinated APC topcoat) via Electrochemical Impedance Spectroscopy[J].Prog Org Coat,2005,52(3):196-209. |
| [20] | Sathiyanarayanan S,Muthkrishnan S,Venkatachari G.Corrosion Protection of Steel by Polyaniline Blended Coating[J].Electrochim Acta,2006,51 (28):6313-6319. |
| [21] | Fahlman M,Jasty S,Epstein A J.Corrosion Protection of Iron/steel by Emeraldine Base Polyaniline:An X-ray Photoelectron Spectroscopy Study[J].Synth Met,1997,85 (1/3):1323-1326. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%