制备了白光OLED器件,器件结构为:ITO/2T-NATA(15 nm)/NPB(25 nm)/ADN:TBPe[(20-x)]nm、ADN:TBPe:DCJFB(x nm)/Alq3(20 nm)/LiF(1 nm)/A14(100 nm).研究了ADN:TBPE:DCJTB层厚度从0~8 nm变化时对器件发光的影响.实验结果表明,当ADN:TBPE:DCJTB层厚度为0时,器件发蓝光;随着ADN;TBPE:DCJTB层厚度的增加,器件发光的色坐标从蓝光区进入白光区,在ADN:TBPE:DCJTB层厚度为6~8 nm时得到色坐标较好的白光器件.
参考文献
[1] | 王琦,马东阁.白光有机发光二极管的制备方法[J].液晶与显示,2009,24(5):617-629. |
[2] | 许运华,彭俊彪,曹镛.白光有机电致发光器件进展[J].化学进展,2006,18(4):389-398. |
[3] | 李志贤,张方辉,赵彦钊,等.LiF作为电子注入层对OLEDs器件性能的影响[J].液晶与显示,2008,23(1):52-57. |
[4] | Cheon K O,Shinar J.Combinatorial fabrication and study of doped layer thickness dependent color evolution in bright small molecular organic light emitting devices[J].Appl.Phys.Lett.,2003,83(10):2073-2075. |
[5] | Andrade B W,Holmes R J,Forrest S R Efficient organic electrophosphorescent white-light-emitting devices with a triple doped emissive layer[J].Adv.Mater.,2004,16(7):624-628. |
[6] | 牛霞,华玉林,吴空物,等.TBPe作蓝光材料的双层白色有机电致发光器件的性能[J].发光学报,2006,27(4):537-542. |
[7] | Tokito S,Lijima T,Tsuzuki T,et al.High-efficiency white phosphorescent organic light-emitting devices with greenish-blue and red-emitting layers[J].Appl.Phys.Lett.,2003,83(12):2459-2461. |
[8] | 吴空物,华玉林,张国辉,等.用于液晶背光源的双层掺杂白光OLED[J].光电子·激光,2007,18(5):515-518. |
[9] | 张春玉,陆景彬,秦莉,等.微腔有机电致发光白光器件设计及制作[J].发光学报,2009,30(5):596-600. |
[10] | 袁桃利,王秀峰,牟强,等.混合型白色有机电致发光器件的研制[J].液晶与显示,2008,23(6):676-679. |
[11] | 滕枫,李扬舟.Poly[(BEHP-PPV)-co-(MEH-PPV)]:DCJTB为功能层LEC器件的能量传递[J].发光学报,2009,30(1)159-62. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%