为了实现溶液化制备有机电致发光器件(OLED),制备和应用具有高溶解性的有机电致发光材料是重要的手段之一。本工作设计和合成了一种含液晶分子中常用的丙基双环己基二氟苯基结构单元的配体及其铱配合物 Ir(cfpp)2(acac)(cfpp =2-(2,3-二氟-5-[trans,trans-4′-丙基-(1,1′-双环己基)]苯基)吡啶);acac =乙酰丙酮负离子)。以其作为绿色发光掺杂材料,按照2%、4%和8%的掺杂含量旋涂制备了 OLED 器件,器件结构为 ITO/PEDOT∶PSS/PVK∶PBD∶Ir(cfpp)2(acac)/ TPBi / LiF / Al。当掺杂浓度为8%时,器件的最大发射波长为524 nm,最大发光亮度达到3600 cd/m2;当电流密度为20 mA/cm2时,最大电流效率和功率效率分别为2.0 cd/A 和0.6 lm/W,具有较强的电致发光特性。研究结果表明,应用含液晶结构单元设计和合成高溶解性的有机电致发光材料是可行的研究思路,为制备可旋涂有机电致发光材料提供了新方法。
In order to realize the fabrication of the OLEDs by solution-processing,synthesis and appli-cation of highly soluble organic electroluminescent materials is one of the important ways.In the pres-ent work,a ligand containing a structural moiety of 4′-n-propyl-(1,1′-bicyclohexyl)-4-difluorophenyl commonly used in liquid crystal molecules and its iridium complex,Ir(cfpp)2 (acac)(cfpp = 2-[2,3-difluoro-5-(trans,trans-4"-n-propyl-(1",1′-bicyclohexyl)-4′-yl)phenylpyridine);acac = acetylaceto-nate)were synthesized.The synthesized iridium complex was used as a green light-emitting dopant material with 2%,4% and 8% doping concentration (mass fraction)in emissive layer to fabricate OLED devices by spin-coating method,and the structure of OLED device comprises of ITO/PEDOT∶PSS/PVK∶PBD∶Ir(cfpp)2 (acac)/ TPBi / LiF / Al.When the doping concentration was 8%,the maximum emission wavelength of OLED device appears at 524 nm with the maximum brightness of 3 500 cd/m2 . When the current density is 20 mA/cm2 ,the maximum current efficiency and power efficiency of the device are 2.0 cd/A and 0.6 lm/W,respectively,indicating that the prepared device shows the inter-esting characteristics of electroluminescence.The obtained results imply that it is a practical concept to design and synthesize the soluble organic electroluminescent materials for spin-coating procedure by introduction of the structural moiety of liquid crystal molecules.
参考文献
[1] | 王梅艳.OLED技术及面临的技术问题探讨[J].现代显示,2006(10):37-40,12. |
[2] | Baldo M A,O′Brien D F,You Y,et al.Highly efficient phosphorescent emission from organic electroluminescent devices [J].Nature,1 998,395(6698):1 5 1-1 54.,1998. |
[3] | 张黎芳 .具有液晶性的新型磷光材料的合成及性能研究[D].四川师范大学,2009. |
[4] | 骆开均,谢明贵,蒋青,李瑛.有机偏振发光材料及其成膜技术研究进展[J].化学研究与应用,2005(03):287-292. |
[5] | 张剑.含噁二唑的吡啶甲酸液晶材料及其环金属铱配合物的合成与光电性能研究[D].湘潭:湘潭大学,2009. Zhang J.The synthesis and properties study of cyclometalated iridium complexes with oxadiazole-based picolinic acid which the liquid-crystal groups were induced into [D].Xiangtan:Xiangtan University,2009.(in Chinese),2009. |
[6] | 张杰,朱旭辉,吴宏滨,黄飞,陈军武,彭俊彪,杨伟,曹镛.溶液加工型有机电致发光材料与器件研究进展[J].中国科学(化学),2013(11):1418-1430. |
[7] | 徐寿颐,吴为民.双环己基多环体系液晶的合成与性质[J].清华大学学报,1 996,36(6):20-25. Xu S Y,Wu W M.Synthesis and properties of liquid crystals with bicyclohexyl multiring systems [J].J ournal of Tsinghua University,1 996,36(6):20-25.(in Chinese),1996. |
[8] | 曹秀英,赵敏,戴修文,闻建勋.双环己基含氟二苯乙炔类负性液晶的合成及应用[J].液晶与显示,2013(06):843-848. |
[9] | Park J C,Park D J,Son K C,et al.The properties of homeotropic alignment materials as the side chain molecular structure in polyimides [J].Molecular Crystals and Liquid Crystals,2007,479(1):1 91/【1229】-203/【1241】.,2007. |
[10] | Xiong Y,Wu J J,Xiao S H.Noncatalytic pyridyl-directed alkylation and arylation carbon-fluorine bond of polyflu-oroarenes with grignard reagents [J].The J ournal of Organic Chemistry,2013,78(9):4599-4603.,2013. |
[11] | 徐茂梁,安忠维,王歌扬,周瑞,肖奇,李明涛,李文连,洪自若.具有减少自猝灭效果的铱配合物掺杂型红色聚合物磷光器件[J].发光学报,2011(11):1181-1185. |
[12] | King S M,Al-Attar H A,Evans R J,et al.The use of substituted iridium complexes in doped polymer electro-phosphorescent devices:The influence of triplet transfer and other factors on enhancing device performance [J]. Advanced Functional Materials,2006,1 6(8):1043-1050.,2006. |
[13] | 王传明,范曲立,霍岩丽,黄维.有机电致磷光材料的分子设计:从主体材料到客体材料[J].化学进展,2006(05):519-525. |
- 下载量()
- 访问量()
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%