概述了研制的钢的环保型防锈颜料(替代铬酸盐)的防锈抑断性能.在3.5%(质量分数)NaCl的中性和酸性水溶液中,对5种常用钢的防锈性能比铬酸盐好;在3.5%NaCl的碱性水溶液中的防锈性比铬酸盐略低;在3.5%NaCl的中性水溶液中,抑制两种常用钢应力腐蚀的能力比铬酸盐高,而抑制腐蚀疲劳断裂(CF)的能力与研制颜料的配方有关.
参考文献
| [1] | Kenjiro Komai .Failure analysis and prevention in SCC and corrosion fatigue cases[J].International Journal of Fatigue,1998(2):145-154. |
| [2] | Woodtli J.;Kieselbach R. .Damage due to hydrogen embrittlement and stress corrosion cracking[J].Engineering failure analysis,2000(6):427-450. |
| [3] | R. Nishimura;Sundjoro .Effects of chromate and molybdate on stress corrosion cracking of type 304 austenitic stainless steel in hydrochloric acid solution[J].Corrosion: The Journal of Science and Engineering,2000(4):361-370. |
| [4] | V. V. Panasyuk;L V. Ratych .Inhibitor Protection of Metals at the Corrosion Fatigue Crack Growth Stage[J].Corrosion: The Journal of Science and Engineering,1995(4):284-294. |
| [5] | RRomagnoli;V F vetere .Non - pollutant Corrosion Inhibitive Pigments: Zinc phosphate, A review[J].Corrosion Reviews,1995,13(01):45-64. |
| [6] | 赵金榜.对环境友好的防锈颜料及作用机理[J].现代涂料与涂装,2002(01):37-39,46. |
| [7] | F. Deflorian;I. Felhosi .Electrochemical Impedance Study of Environmentally Friendly Pigments in Organic Coatings[J].Corrosion: The Journal of Science and Engineering,2003(2):112-120. |
| [8] | S. M. Powell;H. N. McMurray;D. A. Worsley .Use of the scanning reference electrode technique for the evaluation of environmentally friendly, nonchromate corrosion inhibitors[J].Corrosion: The Journal of Science and Engineering,1999(11):1040-1051. |
| [9] | 化学工业部化工机械研究所.腐蚀与防护手册-耐蚀金属材料与防蚀技术分册[M].北京:化学工业出版社,1990:l008-1025. |
| [10] | BFBrown .Stress Corrosion Cracking and Hydrogen Embitterment of Iron and Steel[Z].Nation Association of Corrosion Engineers,1973. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%