合成了含有缩水甘油基、羧基和氨基的三层核壳结构的交联苯丙乳液,研究了中间层厚度、官能团单体用量对乳液性能及其涂膜性能的影响,当中间层投料量为核壳层的50%,官能团单体甲基丙烯酸缩水甘油酯(GMA)、甲基丙烯酸(MAA)和甲基丙烯酸二甲氨基乙酯(DMEMA)分别为各层投料量的3%、1.5%和3%时,乳液有最佳的综合性能.用该乳液制备的水性防锈涂料与普通苯丙乳液相比具有更好的防锈性能,涂膜耐3%盐水浸泡时间达624 h.
参考文献
[1] | Reyes Y;Rodriguez FJ;del Rio JM;Corea M;Vazquez F .Characterisation of an anticorrosive phosphated surfactant and its use in water-borne coatings[J].Progress in Organic Coatings: An International Review Journal,2005(4):366-371. |
[2] | Sharmin E;Imo L;Ashraf SM;Ahmad S .Acrylic-melamine modified DGEBA-epoxy coatings and their anticorrosive behavior[J].Progress in Organic Coatings: An International Review Journal,2004(1):47-54. |
[3] | PARK J H;LEE G D;NISHIKATA A et al.Anticorrosive behavior of hydroxyapatite as an environmentally friendly pigment[J].Corrosion Science,2002,44(01):1087-1095. |
[4] | B DEL AMO;ROMAGNOLI R;DEYA C et al.High performance water-based paints with non-toxic anticorrosive pigments[J].Progress in organic Coatings,2002,45(01):389-397. |
[5] | POKHMURS'KYI V I;ZIN' I M;LYON S B .Inhibition of corrosion by a mixture of nonchromate pigments in organic coatings on galvanized steel[J].Materials Science,2004,40(03):383-390. |
[6] | 危恒毅,岳庆磊,宋晓锐,杨辉荣.水性防腐涂料体系[J].精细石油化工进展,2002(04):44-46. |
[7] | 郭清泉,林淑英,陈焕钦.水性金属防腐蚀涂料所用基料现状及发展[J].现代化工,2003(10):25-27,32. |
[8] | IVANCHEV S S;PAVLYUCHENKO V N;BYRDINA N A et al.Water-resistant films and coatings based on cross-linking styrene-acrylate latex copolymers[J].Russian Journal of Applied Chemistry,2001,74(02):309-315. |
[9] | 崔秀兰,郭俊文,张宇飞,王培燕.水性防腐涂料用苯丙乳液的制备工艺研究[J].内蒙古工业大学学报(自然科学版),2002(02):103-108. |
[10] | 吴道新,肖忠良,胡飞.St/BA/AN水性防腐涂料的研制[J].现代涂料与涂装,2004(02):19-20,24. |
[11] | 余樟清,李伯耿,潘祖仁.GAD室温自交联乳液的合成及其涂膜性能[J].功能高分子学报,2001(04):456-460. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%