采用钼酸铵(AM)、可膨胀石墨(EG)和AM/EG对三聚氰胺聚磷酸盐(MPP)/三聚氰胺(MEL)/季戊四醇(PER)超薄型防火涂料进行改性,制备改性涂料.耐火性能测试、TGA分析表明,与EG改性相比,AM、EG协同改性延长了耐燃时间,提高了残炭量.采用Freeman方法计算了防火涂料的热降解活化能,AM/EG改性较EG改性的防火涂料在200～330℃、330～500℃阶段的活化能分别提高了59.72 kJ/mol和67.71 kJ/mol,AM/EG改性防火涂料防火性能好.
参考文献
| [1] | M JIMENEZ;S DUQUESNE;S BOURBIGOT .Intumescent fire protective coating:towards a better understanding of their mechanism of action[J].Thermochimica Acta,2006,449(1-2):16-26. |
| [2] | Jun-wei Gu;Guang-cheng Zhang;Shan-lai Dong;Qiu-yu Zhang;Jie Kong .Study on preparation and fire-retardant mechanism analysis of intumescent flame-retardant coatings[J].Surface & Coatings Technology,2007(18):7835-7841. |
| [3] | Zhenyu Wang;Enhou Han;Wei Ke .Influence of expandable graphite on fire resistance and water resistance of flame-retardant coatings[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2007(5):2237-2253. |
| [4] | 刘学军,付若愚,咸才军,郭保文,郭奋.可膨胀石墨在膨胀型钢结构防火涂料中的应用[J].精细化工,2005(05):328-330,341. |
| [5] | 张龙,王建祺.新型无卤可膨胀石墨防火涂料[J].北京理工大学学报,2001(05):649-652. |
| [6] | 王震宇,韩恩厚,柯伟.可膨胀石墨改性APP/PER/EN防火涂料热降解行为[J].复合材料学报,2005(05):52-59. |
| [7] | 李国新,梁国正,杨秦莉,宋学锋.可膨胀石墨改性APP/PER/MEL防火涂料的热降解研究[J].涂料工业,2006(11):11-14,18. |
| [8] | 吕九琢,徐亚贤,竺栋荣,张雳.IFRC-871饰面膨胀型防火涂料的研制[J].石油化工高等学校学报,2001(04):35-39. |
| [9] | 杨秦莉,李国新,周文英,何廷树.MoO3对膨胀型防火涂料残炭的影响[J].涂料工业,2006(05):24-28. |
| [10] | 覃文清,戚天游.在防火涂料中加入LL阻燃剂的热解反应[J].化工学报,2004(03):450-454. |
| [11] | 徐晓楠,周亮,陈南,郑兰芳,王平.KFR-2特种饰面型防火涂料的热解动力学分析[J].安全与环境学报,2005(03):95-97. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%