筛选了最佳表面处理剂为硅烷偶联剂(KH570),研究了偶联剂用量、pH值、时间等因素对纳米TiO2有机化表面改性的影响.采用亲油化度实验、红外光谱、透射电镜等手段表征了纳米二氧化钛的改性效果和结构.实验结果表明:KH570以化学键合的形式结合于纳米TiO2表面,当硅烷偶联剂用量为10%、pH值为6.5、处理时问为1.0-1.5 h时,TiO2的有机化表面改性效果最好,TiO2在乙醇中达到纳米级的分散.
参考文献
| [1] | 蒋子铎,吴璧耀,刘安华.二氧化钛的表面化学改性[J].武汉化工学院学报,1991(02):1-8. |
| [2] | Li ZW.;Zhu YF. .Surface-modification of SiO2 nanoparticles with oleic acid[J].Applied Surface Science: A Journal Devoted to the Properties of Interfaces in Relation to the Synthesis and Behaviour of Materials,2003(1/4):315-320. |
| [3] | B J PARK;J Y LEE .Microcapsules containing electrophoretic suspension of TiO2 modified with poly(methyl methacrylate)[J].Current Applied Physics,2006,6(04):632-635. |
| [4] | Masayoshi Fuji;Takashi Takei;Tohoru Watanabe;Masatoshi Chikazawa .Wettability of fine silica powder surfaces modified with several normal alcohols[J].Colloids and Surfaces, A. Physicochemical and Engineering Aspects,1999(1/2):13-24. |
| [5] | 姚超,丁永红,林西平,杨绪杰,陆路德,汪信.纳米TiO2有机表面改性的研究[J].无机化学学报,2005(05):638-642. |
| [6] | 陈云华,林安,甘复兴.纳米TiO2的改性及其在丙烯酸涂料中的应用[J].腐蚀科学与防护技术,2007(01):58-60. |
| [7] | 孙镛,毕研迎,石凤.TiO2-双亲共聚物复合纳米粒子的合成与紫外光敏特性[J].化学学报,2007(01):67-71. |
| [8] | 李晓娥,邓红,张粉艳,樊安,任云霞,文红梅,祖庸.纳米二氧化钛有机化改性工艺研究[J].无机盐工业,2001(04):5-7. |
| [9] | NOLLW.Chemistry and Technology of Silicones[M].London,UK:Academic Press,1968 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%