电化学方法测试涂层防护性能较之于常规的方法如场地曝晒、盐雾试验、盐水浸泡、干湿循环试验等有许多优点:测试方便快捷,破坏少,获得与涂层防护性能相关的直接信息量大,同时能对金属的腐蚀机理及涂层失效行为进行更深入的研究.本文参考近年来国内外相关文献,对检测涂层防护性能的电化学方法做了总结,综述了直流法、电化学阻抗谱法、电化学噪声法、扫描开尔文探针及扫描振动电极等技术在检测涂层防护性能方面的应用.
参考文献
[1] | 曹楚南.悄悄进行的破坏[M].北京:清华大学出版社,2000 |
[2] | 丁长旺.几项涂层性能测试方法简介[J].涂料工业,2005(06):59-61. |
[3] | 张丽,牛明军,刘雪莹,刘大壮,庞勇.水性防锈涂料的配方筛选及防锈性能研究[J].高分子材料科学与工程,2005(01):260-263. |
[4] | Chen WB.;Chen P.;Chen HY.;Wu J.;Tsai WT. .Development of Al-containing zinc-rich paints for corrosion resistance[J].Applied Surface Science: A Journal Devoted to the Properties of Interfaces in Relation to the Synthesis and Behaviour of Materials,2002(1/2):154-164. |
[5] | 钟富荣.断电电位和涂层面电阻率测试方法[J].油气储运,2002(06):36-38,46. |
[6] | A. Bouyanzer;B. Hammouti;L. Majidi .Pennyroyal oil from Mentha pulegium as corrosion inhibitor for steel in 1 M HCl[J].Materials Letters,2006(23):2840-2843. |
[7] | M. Elayyachy;A. El Idrissi;B. Hammouti .New thio-compounds as corrosion inhibitor for steel in 1 M HCl[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2006(9):2470-2479. |
[8] | Ouchrif A;Zegmout M;Hammouti B;Dafali A;Benkaddour M;Ramdani A;Elkadiri S .New synthesised diamine derivatives as corrosion inhibitors of steel in 0.5 M H2SO4[J].Progress in Organic Coatings: An International Review Journal,2005(4):292-296. |
[9] | Y. Y. Chen;S. C. Chung;H. C. Shih .Studies on the initial stages of zinc atmospheric corrosion in the presence of chloride[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2006(11):3547-3564. |
[10] | P PERNICE;M ARPAIA;A COSTANTINI .Steel corrosion rate in soils by a.c.and d.c.electrochemical methods[J].Materials Chemistry and Physics,1990,26(3-4):323-330. |
[11] | M.A. Pech-Canul;P. Castro .Corrosion measurements of steel reinforcement in concrete exposed to a tropical marine atmosphere[J].Cement and Concrete Research,2002(3):491-498. |
[12] | B LENGYEL;L.MESZAROS;G MESZAROS et al.Electrechemical methods to determine the corrosion rate of a metal protected by a paint film[J].Progress in Organic Coatings,1999,36(1-2):11-14. |
[13] | G ROCCHINI .A theoretical study of the influence of the ohmic drop on polarization curves[J].Corrosion Science,1996,38(04):655-668. |
[14] | ASTM G106-1989.ASTM G106-1989.Standard practice for verification of algorithm and equipment for electrochemical impedance measurements[S]. |
[15] | C CORFIAS;N PEBERE;C LACABANNEB .Characterization of protective coatings by electrochemical impedance spectroscopy and a thermostimulated current method:in nence of the polymer binder[J].Corrosion Science,2000,42(08):1337-1350. |
[16] | Rosales BM;Di Sarli AR;de Rincon O;Rincon A;Elsner CI;Marchisio B .An evaluation of coil coating formulations in marine environments[J].Progress in Organic Coatings: An International Review Journal,2004(2):105-114. |
[17] | S. Sathiyanarayanan;S. Muthkrishnan;G. Venkatachari .Corrosion protection of steel by polyaniline blended coating[J].Electrochimica Acta,2006(28):6313-6319. |
[18] | Lendvay-Gyorik G;Pajkossy T;Lengyel B .Corrosion-protection properties of water-borne paint coatings as studied by electrochemical impedance spectroscopy and gravimetry[J].Progress in Organic Coatings: An International Review Journal,2006(4):304-310. |
[19] | D J BACON;D GAVILLET;A HORSEWELL et al.Summary of montreux workshop on time dependence of radiation damnge accumulation and its impact on materials properties[J].Journal of Nuclear Materials,1993,206(2-3):368-371. |
[20] | 吴丽蓉,胡学文,许崇武.用EIS快速评估有机涂层防护性能的方法[J].腐蚀科学与防护技术,2000(03):182-184. |
[21] | M. Mahdavian;M.M. Attar .Another approach in analysis of paint coatings with EIS measurement: Phase angle at high frequencies[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2006(12):4152-4157. |
[22] | 张鉴清,张昭,王建明,成少安,曹楚南.电化学噪声的分析与应用Ⅱ.电化学噪声的应用[J].中国腐蚀与防护学报,2002(04):241-248. |
[23] | CHEN;SKERRY.Assessing the corrosion resistance of painted steel by AC impedance and eleetrochmieal noise techniques[J].Corrosion,1991(47):598-611. |
[24] | Y. Puget;K. Trethewey;R. J. K. Wood .Electrochemical noise analysis of polyurethane-coated steel subjected to erosion-corrosion[J].Wear: an International Journal on the Science and Technology of Friction, Lubrication and Wear,1999(0):552-567. |
[25] | BIERWAGEN GP.Calculation of noise resistancefromsimultaneous electrochemical voltage and current noise data[J].Eleetroehem Sec,1994(141):155-157. |
[26] | Greisiger H.;Schauer T. .On the interpretation of the electrochemical noise data for coatings[J].Progress in Organic Coatings: An International Review Journal,2000(1 SpecialIssueSI):31-36. |
[27] | S MABBUTT;D J MILLS;C P WOODCOCK.Developments of the electrochemical noise method(ENM)for more practical assessment of anti-corrosion coatings[J].Progress in Organic Coatings,2006:1-5. |
[28] | W FIüRBETH;M STRATMANN .The delamination of polymeric coatings from electrogalvanized steel-a mechanistic approach.part 2:delamination from a defect down to steel[J].Corrosion Science,2001,43(02):229-241. |
[29] | W FORBETH;M STRATMANN .The delamination of polymeric coatings from electragalvanized steel-a mechanistic approach.part 3:delamination kinetics and influence of CO2[J].Corrosion Science,2001,43(02):243-254. |
[30] | K. Wapner;M. Stratmann;G. Grundmeier .In situ infrared spectroscopic and scanning Kelvin probe measurements of water and ion transport at polymer/metal interfaces[J].Electrochimica Acta,2006(16):3303-3315. |
[31] | J.H.W.Wit;D.H.Weijde .Local measurements in electrochemistry and corrosion technology[J].Materials Science Forum,1998(Pt.1):69-76. |
[32] | E.Bayet;F.Huet .Adaptation of the scanning vibrating electrode technique to ac mode: local electrochemical impedance measurement[J].Materials Science Forum,1998(Pt.1):57-68. |
[33] | F.Zou;C.Barreau .Application of scanning vibrating electrode techniques to study the degradation of coil-coated steel at edges[J].Materials Science Forum,1998(Pt.1):83-92. |
[34] | Zin IM;Lyon SB;Hussain A .Under-film corrosion of epoxy-coated galvanised steel - An EIS and SVET study of the effect of inhibition at defects[J].Progress in Organic Coatings: An International Review Journal,2005(2):126-135. |
[35] | JIE HE;DENNIS E TALLMAN;GORDON P BIERWAGEN .Conjagated polymers for corrosion control:scanning vibrating electrode studies of polypyrrole-aluminum alloy interactions[J].Electrochemical Society,2004,151(12):644-13651. |
[36] | Zubielewicz M;Gnot W .Mechanisms of non-toxic anticorrosive pigments in organic waterborne coatings[J].Progress in Organic Coatings: An International Review Journal,2004(4):358-371. |
[37] | B VUILLEMIN;X PHILIPPE;R OLTRA et al.SVET,AFM and AES study of pitting corrosion initiated on MnS inclusions by microinjection[J].Corrosion Science,2003,45(06):1143-1159. |
[38] | 郭清泉,陈焕钦.金属腐蚀与涂层防护[J].合成材料老化与应用,2003(04):36-39. |
[39] | 徐峰;邹候招;储建.环保型无机涂料[M].北京:化学工业出版社,2004 |
[40] | 刘斌,孟繁强,尚永春.原子力显微镜在涂层分析中的应用[J].涂料工业,2000(02):38-40. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%