通过丙烯酸甲酯和乙二醇胺的Michael加成反应,制得了AB2型单体/N,N'-二羟乙基-3-氨基丙烯酸甲酯,通过添加核单体和采用"准一步法"的合成途径,制备了端羟基超支化聚)酯-胺),通过丙烯酸对该聚合物进行改性反应,得到了端丙烯酸酯基的超支化聚合物,研究了改性聚合物与内烯酸异冰片酯的紫外光固化涂层性能.
参考文献
[1] | FLORY PJ.Molecular size distribution in three dimensional polymers[J].Journal of the American Chemical Society,1952(74):2718-2724. |
[2] | KMYH WEBSTER OW .Hyperbranehed polyphenyl-enes[J].Macr Omolecules,1992,25(21):5561-5572. |
[3] | KIM YH;WEBSTER OW.Hyperbranehed polyphenylene[J].Macromolecules,1992(25):5561-5572. |
[4] | HAWKER CJ;LEE L;FRECHET JMJ.One-step synthesis of hyperbranched dendrition polyesters[J].Journal of the American Chemical Society,1991(113):4583-4588. |
[5] | SUZUKI M;II A;SAEGUSA T.Multibranehing polymerization:palladium-catalyzed ring polymerization of cyelie carbamate to produce hyperbranched dendritie polyamine[J].Macromolecules,1992(25):7071-7072. |
[6] | SPINDLER R;FRECHET JMJ.Synthesis and characterization of hyperbranehed polyurethanes prepared from blocked isocyanate monomers by step-growth polymerization[J].Macromolecules,1992(26):4809-4813. |
[7] | KUMAR A;RAMAKRISHNAN S .Hyperbranehed polyurethanes with varying spacer segments between the branching points[J].Polymer Chemistry,1993,34(05):839-848. |
[8] | Bolton DH.;Wooley KL. .SYNTHESIS AND CHARACTERIZATION OF HYPERBRANCHED POLYCARBONATES[J].Macromolecules,1997(7):1890-1896. |
[9] | UHRICH KE;HAWKER CJ;FRECHET JMJ.One-pot synthesis of hyperbranehed polyethers[J].Macremolecules,1992(25):4583-4587. |
[10] | 张晓龙,唐黎明,付永柱,刘德山,邱藤.新型芳香型超支化聚酯的合成与应用研究[J].高等学校化学学报,2001(10):1761-1763. |
[11] | WEI H Y;KOU H G;SHI W F et al.Influence of reactive diluent on UV-during of acrylate terminated hyperbranded polymers[J].Journal of Coatings Technology,2003,75(939):37-40. |
[12] | 唐黎明,张晓龙,李伟,刘德山.脂肪型超支化聚酯的端基改性研究[J].高等学校化学学报,2000(12):1950. |
[13] | 唐黎明.新型功能性超支化聚酯的合成及表征[J].高等学校化学学报,2001(06):1073-1075. |
[14] | ROLF ATM;BENTHEM V.Novel hyperbranehed resins for coating applications[J].Progress in Organic Coatings,2000(40):203-214. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%