采用乳液型丙烯酸树脂为主要成膜物,水稀释性羟基硅丙树脂为改性剂,甲基醚化三聚氰胺树脂为固化剂,制备了性能优异的水性氨基烘烤涂料.当固化剂与成膜树脂的质量比为1:4,改性剂占成膜树脂总量的16.7%,颜料体积浓度为18%时,漆膜的硬度为2H,耐冲击性为50 cm,60°光泽>90,附着力1级,耐乙醇性好.并采用红外光谱分析了其固化前后分子结构及变化.
参考文献
| [1] | 涂伟萍;夏正斌;边蕴静.水分散体涂料[M].北京:中国轻工业出版社,2004:222-232. |
| [2] | WATSON B C;WIEKS JRZW .Popping of water-soluble acrylic coatings[J].Journal of Coatings Technology,1983,55(698):59-65. |
| [3] | HILL L W;RIEHARDS B M .Viscosity of eosolvent/water solutions of amine neutralized acrylic copolymers[J].J Coat'Technol,1979,51(654):59-67. |
| [4] | STANLEY K NICKLE;ERVIN R WERNER .Waterbased coating composition of methylol(meth)acrylamide acrylic polymer,acrylic hydrosol and melamine emsslinking agent[P].US,5221584,1993-06-22. |
| [5] | STANLEY K NICKLE;ERVIN R WERNER .Water-based coating compositions of methylol(meth)acrylamide acrylic aolymer,polyurethane and melamine crosslinking agent[P].US,5314945,1994-05-24. |
| [6] | 李江年,王德智,张梅,唐林生.改性氨基丙烯酸乳胶漆的研制[J].涂料工业,2003(06):3-6. |
| [7] | 武利民,钱峰,游波,李丹.热固性树脂交联密度的测定[J].高分子材料科学与工程,2001(06):75-77. |
| [8] | 牛广轶,刘康.涂料用氨基树脂的进展--甲醚化氨基树脂[J].现代涂料与涂装,2000(06):38-40. |
| [9] | 毕胜.中国钛白工业与涂料[J].现代涂料与涂装,2003(02):41-43. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%