为了克服钢结构防火涂料膨胀发泡层蓬松易脱落和易开裂的缺点,采用可膨胀石墨来改善防火涂料发泡层的结构.研究了可膨胀石墨对发泡层形貌和钢结构耐火极限的影响.结果表明,可膨胀石墨膨胀后成"蠕虫"状穿插于发泡层中,起到增强作用,使炭质层结构更致密.采用膨胀容积为180 mL/g、粒径为0.18 mm、起始膨胀温度为150 ℃的可膨胀石墨时,当添加量为3%时具有较好的改性作用.
参考文献
| [1] | 于梅,陈玉婷.膨胀石墨特性浅析及其在阻燃方向的应用前景[J].廊坊师范学院学报,2002(04):70-72. |
| [2] | 曹乃珍;沈万慈;温诗铸 .膨胀石墨微观孔结构的特点及其表征[J].物理化学学报,1996,12(08):766-768. |
| [3] | 任京城;沈万慈;杨赞中 等.膨胀石墨--一种新型环境材料[J].中国非金属矿工业导刊,1999,9(03):25-26. |
| [4] | M. Le Bras;S. Bourbigot .Comprehensive study of the degradation of an intumescent EVA-based material during combustion[J].Journal of Materials Science,1999(23):5777-5782. |
| [5] | 杨卫疆,诸秋萍,陆亨荣,林桂祥.膨胀型防火涂料炭化层形成过程的探讨[J].化学建材,2001(06):20-23. |
| [6] | Duquesne S.;Bourbigot S.;Delobel R.;Camino G.;Eling B. Lindsay C.;Roels T.;Le Bras M. .Thermal degradation of polyurethane and polyurethane/expandable graphite coatings[J].Polymer Degradation and Stability,2001(3):493-499. |
| [7] | M. Modesti;A. Lorenzetti;F. Simioni .Expandable graphite as an intumescent flame retardant in polyisocyanurate-polyurethane foams[J].Polymer Degradation and Stability,2002(2):195-202. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%