采用分步聚合方法合成了P(MMA-co-AA-co-HEMA)/P(BMA-co-HEMA)半互穿聚合物网络水溶胶,在MMA网络中加入交联剂二乙烯基苯(DVB),在BMA网络中不加入交联剂.用动态黏弹谱DMA(Dynamic Mechanical Analysis)分析水溶胶的阻尼性能并测试其涂膜5项性能指标.实验发现当m(MMA):m(BMA)=5:5,w(DVB)=0.1%,PMMA/PBMA半IPN可同时满足阻尼性能和涂膜性能的基本要求.同时涂膜力学阻尼能力经力学振动阻尼测定装置检测,振幅衰减明显.而且振动阶数越高,阻尼效果越好.
参考文献
| [1] | 何曼君;陈维孝;董西侠.高分子物理[M].上海:复旦大学出版社,2004:348. |
| [2] | Hu, R;Dimonie, VL;ElAasser, MS;Pearson, RA;Hiltner, A;Mylonakis, SG;Sperling, LH;LEHIGH UNIV,INST EMULS POLYMERS,BETHLEHEM,PA 18015.;LEHIGH UNIV,DEPT CHEM,BETHLEHEM,PA 18015.;LEHIGH UNIV,DEPT MAT SCI & ENGN,BETHLEHEM,PA 18015. .Multicomponent latex IPN materials .1. Morphology control[J].Journal of Polymer Science. Part A, Polymer Chemistry,1997(11):2193-2206. |
| [3] | HU R;DIMONIE V L;ELAASSER M S et al.Multicomponent latex IPN materials:2.damping and mechanical behavior[J].J Polym Sci Part B Polymer Physics,1997,35:1501-1514. |
| [4] | M. S. El-Aasser;R. Hu;V. L. Dimonie;L. H. Sperling .Morphology, design and characterization of IPN-containing structured latex particles for damping applications[J].Colloids and Surfaces, A. Physicochemical and Engineering Aspects,1999(1/3):241-253. |
| [5] | K. I. Suresh;S. Vishwanatham;E. Bartsch .Viscoelastic and damping characteristics of poly (n-butyl acrylate)-poly(n-butyl methacrylate) semi-IPN latex films[J].Polymers for Advanced Technologies,2007(5):364-372. |
| [6] | 万里鹰;肖凌.IPN的研究进展[J].高分子材料科学与工程,1999(02):4-9. |
| [7] | 万里鹰,徐泳文,卢金山,王高潮,李卓美."核--壳"IPN型聚丙烯酸酯类阻尼涂膜综合性能[J].南昌航空大学学报（自然科学版）,2007(04):43-48,77. |
| [8] | 万里鹰,王高潮,江洪流,卢金山,李卓美.聚丙烯酸酯类材料的阻尼性能研究[J].南昌航空大学学报（自然科学版）,2008(02):68-72. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%