以自制不同相对分子质最的聚已二酸-新戊二醇酯二醇(PNA型聚酯二醇)和异佛尔酮二异氰酸酯(IP-DI)为主要原料,二羟甲基丙酸(DMPA)为亲水单体,水合肼为扩链剂,制备了IPDI型的水性聚氨酯乳液.研究了PNA聚酯二醇相对分子质量对IPDI型预聚体黏度和水分散性的影响.实验结果表明,将PNA聚酯二醇的相对分子质量控制在1 400以下时,用低相对分子质量的PNA与IPDI的预聚体具有黏度低、易于水分散的特点,可以实现水分散时不加或少加有机溶剂降黏的目的;利用万能材料试验机、XRD、FT-IR和差示扫描量热仪等仪器对所得乳液成膜物的力学性能进行了测试,结果表明:用低相对分子质量的(＜1 400)PNA合成的IPDI型乳液的成膜物力学性能可以满足应用的要求.
IPDI-based waterborne polyurethane (WPU) were synthesized by using PNA type of polyester diols with different molecular weight and IPDI as raw materials,dimethylol propionic acid (DMPA) as hydrophilic monomer and hydrazine hydrate as chain-extender.The influence of different molecular weight polyester diols on the viscosity and water dispersibility of IPDI-based prepolymer were studied.The results indicated that IPDI prepolymer have low viscosity and good water dipersibility by using low molecular weight PNA (M_n under 1 400),water dispersion can be obtained with less or without organic solvent.The mechanical properties of the WPU films was studied by using all-purpose materials tester,XRD,IR and DSC instrument.The results indicated that the mechanical properties of the WPU films are better and could meet the needs of the users.
参考文献
| [1] | 孙彦璞,任孝修.低粘度水性聚氨酯预聚体[J].涂料工业,2003(04):32-34. |
| [2] | 吕维忠.脂肪族水性聚氨酯树脂的合成与性能研究[J].涂料工业,2003(02):35-37. |
| [3] | 李绍雄;刘益军.聚氨酯树脂及其应用[M].北京:化学工业出版社,2002 |
| [4] | 任彦强 .TMXDI型聚氨酯分散体的合成与性能研究[D].北京:北京化工大学,2000. |
| [5] | Ten-Chin Wen;Yeong-Jyh Wang;Tsung-Tien Cheng;Chien-Hsin Yang .The effect of DMPA units on ionic conductivity of PEG-DMPA-IPDI waterborne polyurethane as single-ion electrolytes[J].Polymer: The International Journal for the Science and Technology of Polymers,1999(14):3979-3988. |
| [6] | 吕维中;刘波;韦少慧 .水性聚氨酯胶膜耐水性的研究[J].皮革科学与工程,2006,2(16):50-54. |
| [7] | 胡剑青,涂伟萍,瞿金清,陈焕钦.聚酯型水性聚氨酯合成工艺[J].华南理工大学学报(自然科学版),2002(04):73-76. |
| [8] | LAN P N;CORNEILM S;SCHACHT E.Synthesis and characterization of segmented polyurethanes based on amphiphilic palyether diols[J].Biomateriai,1996(17):2237-2280. |
| [9] | YOUNG-KUK JHON;IN-WOO CHEONG .Chain extension study of aqueous polyurethane dispersion[J].Colloids and Surfaces A:Physicochemical and Engineering Aspects,2001,179:71-78. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%