以异佛尔酮二异氰酸酯(IPDI)、聚氧化丙烯二醇(PPG)、二羟甲基丙酸(DMPA) 为主要原料,用4%的环氧树脂和3%的氨基硅烷复合改性合成了有机硅改性环氧-聚氨酯乳液,乳液外观呈黄白色且具有较好的稳定性.用红外光谱仪、接触角测定仪、热重分析仪对涂膜的结构和性能进行了检测,结果表明:聚合物中因环氧树脂的交联作用和Si-O键的存在,涂膜表面憎水性增强、耐水性和耐热性得到提高.
The epoxy-polyurethane emulsion Modified by Silicone was synthesized using isophorone diisocyanate(IPDI), polydiol(PPG), dimethoxypropionic acid(DMPA) as main raw materials,which was further modified with 4 percent of epoxy resin and 3 percent of amino silane. The obtained yellowish white emulsion showed good stability. The structure and properties of the coating was characterized by IR, contact angle and TG. The results showed that the hydrophobicity, water resistance and heat resistance of coating was enhanced due to the introduction of Si-O bond and the crosslinking of epoxy resin.
参考文献
| [1] | 朱晓丽,张庆思,冯圣玉.有机硅改性水性聚氨酯的研究进展[J].中国皮革,2005(03):42-44. |
| [2] | 杨清峰,瞿金清,陈焕钦.有机硅改性水性聚氨酯的研究进展[J].涂料技术与文摘,2004(06):1-5. |
| [3] | 易翔,何德良,吴振军,何莉萍.环氧改性水性聚氨酯乳液合成及其性能研究[J].现代涂料与涂装,2009(05):13-15,22. |
| [4] | 佘文骊.硅烷偶联剂封端改性水性聚氨酯的研究[J].中国胶粘剂,2008(06):10-14. |
| [5] | JAND WONSEO;BYNG KYUKIM .Preparations and properties of waterborne polyurethane/nanosilica composition[J].Polymer Bulletin,2005,5(04):123-128. |
| [6] | 井新利;于洁.有机硅偶联剂在新材料中的一些特殊用途[J].化学通报(印刷版),1996(02):26-28. |
| [7] | Mequanint K.;Sanderson R. .Self-assembling metal coatings from phosphated and siloxane-modified polyurethane dispersions: An analysis of the coating-air interface[J].Journal of Applied Polymer Science,2003(4):893-899. |
| [8] | 幸松民;王一璐.有机硅合成工艺及产品应用[M].北京:化学工业出版社,2000:331-342. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%