采用十八胺与乙二醇二缩水甘油醚反应,制得一种两端为环氧基,中间氮原子上接有长疏水烷基链的功能性双环氧基化合物,再用脂三乙烯四胺对该化合物进行封端,制得一种非离子型水性环氧固化剂.研究表明:由于该固化剂具有疏水效果的长烷基链和亲水效果的羟基、胺基、醚键,从而使得该固化剂具有表面活性剂的结构.因此相对其他水性固化剂来讲,该固化剂不仅仅不需要采用中和剂就具有亲水性,且其对环氧树脂有良好的乳化效果.该固化剂与液体环氧树脂所制备的双组分室温固化涂膜性能优良,具有优异的铅笔硬度、耐冲击性和耐化学性.同时该固化剂含有较长的柔性烷基链,所以固化后的环氧树脂将有较好的柔韧性.
参考文献
| [1] | GLASS JE.Technology for waterborne coatings[M].Washington,DC:American Chemical Society,1997:15-18. |
| [2] | 李士强,张亚峰,邝健政,徐宇亮.阳离子型水性环氧树脂灌浆材料的制备[J].新型建筑材料,2009(01):53-57. |
| [3] | SHIMP;DAIID A;HICKS et al.Two component aqueous coating composition based on ane poxy-polyamine adduct and a polyepoxide[P].US,4246148,1981-01-20. |
| [4] | Jim D.Elmore;Derek S.Kincaid;Pratap C.Komar .Waterborne epoxy protective coatings for metal[J].JCT,2002(931):63-72. |
| [5] | KLEIN;DIETER H;WESSELY et al.Water compatible amine terminated resin useful for curing epoxy resins[P].US,5567748,1996-10-22. |
| [6] | STARK;CHARLES J;BACH et al.Epoxy-functional amidoamine reacted with excess polyamine and monoepoxy as epoxy curative[P].US,6277928,2001-08-21. |
| [7] | GERLITZ;MARTIN;FISCHER et al.Water dilutable amine curing agents for aqueous two component epoxy resin systems[P].US,6653369,2003-11-25. |
| [8] | 周继亮,涂伟萍.非离子型自乳化水性环氧固化剂的合成与性能[J].高校化学工程学报,2006(01):94-99. |
| [9] | 张兰芬,周秀丽.环氧固化剂胺值的测定[J].涂料技术与文摘,2004(01):40-41. |
| [10] | 谭振,周振强,刘平平,苏建华,安海龙.环保型汽车用水性环氧树脂底漆的研制[J].上海涂料,2009(03):9-11. |
| [11] | 王丰 .水性环氧树脂涂料固化剂的合成及性能研究[D].湖南大学,2004. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%