在碱性条件下合成出导电聚苯胺粉末,测定了聚苯胺的红外光谱、电导率、粒径分布、极化曲线及电化学阻抗谱.结果表明,当pH为12.18时,电导率可达到8.35×10-2 S/cm;聚苯胺粉末粒径分布范围为0.44～43.57 μm;聚苯胺涂层可使钢铁的腐蚀电位正移,腐蚀电流密度下降,阻抗值变大,提高了钢铁的防腐蚀性能.
参考文献
| [1] | 王刚,刘维锦.聚苯胺改性涂料的防腐性能研究[J].涂料工业,2008(07):1-3,6. |
| [2] | 孙毅,钟发春,舒远杰,郝晓飞,刘勇.聚苯胺涂层防腐行为的电化学研究方法[J].电镀与涂饰,2009(08):62-66. |
| [3] | 张金勇,李季,王献红,景遐斌,王佛松.聚苯胺在防腐领域的应用[J].功能高分子学报,1999(03):350-356. |
| [4] | Schauer T.;Dulog L.;Eisenbach CD.;Joos A. .Protection of iron against corrosion with polyaniline primers [Review][J].Progress in Organic Coatings: An International Review Journal,1998(1):20-27. |
| [5] | Xing Wang;Na Liu;Xue Van;Wanjin Zhang;Yen Wei .Alkali-guided Synthesis of Polyaniline Hollow Microspheres[J].Chemistry Letters,2005(1):42-43. |
| [6] | MACDIARMID A G;CHIANG J C;RICHTER A F et al.Polyaniline:A new concept in conducting polymers[J].Synthetic Metals,1987,18(1/3):285-290. |
| [7] | 刘东杰,王云普,高敬民,李玉峰,郭晓芳.环保型水性沥青环氧树脂防腐涂料[J].涂料工业,2006(06):30-32,36. |
| [8] | 李玉峰 .聚苯胺/蒙脱土复合防腐蚀涂层的制备及性能研究[D].西北师范大学,2005. |
| [9] | Castela A.S.L.;Simoes A.M. .E.I.S. evaluation of attached and free polymer films[J].Progress in Organic Coatings: An International Review Journal,2000(1):1-7. |
| [10] | 俞敦义;史铁京 .TU涂料的耐蚀性能研究[J].涂料工业,1997,27(06):12-13. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%