以异佛尔酮二异氰酸酯(IPDI)、六亚甲基二异氰酸酯(HDI)、聚己二酸丁二醇酯(PBA)为主要原料合成了水性聚氨酯乳液,并通过FT-IR、DSC、粒径分析表征手段,研究了硬段组成中HDI和IPDI的相对含量对乳液及成膜性能的影响.结果表明:随着HDI 含量的增加,乳液粒径变大,粒径分布变窄,乳胶粒子的ξ电位变小,乳液稳定性变差,HDI含量的增加促使了软硬两相的结晶;HDI规整的线型结构提高了聚氨酯胶膜的柔韧性,随着HDI含量的增加,断裂伸长率增大,拉伸强度降低,吸水率降低,但在HDI含量过高时,增加了软硬两相的相容性,吸水率出现微弱的上升.
参考文献
| [1] | TOBOLSKY A V .Properties of linear elastomeric polyurethane[J].Journal of Applied Polymer Science,1996,10(12):1837-1844. |
| [2] | D. Roy;R. Chen;P. Callaghan .Study of bond strengths of a water-borne polyurethane (PU) adhesive for shoe-soling materials[J].The Journal of the Textile Institute, Part 3. Technologies for a New Century,2005(1):17-20. |
| [3] | F. Rezaei;F. Sharif;A. A. Sarabi .Evaluating water transport through high solid polyurethane coating using the EIS method[J].JCT research,2010(2):209-217. |
| [4] | KUMAN S;MISHRA A K;DIPAK K et al.Synthesis and charaeterization of hyperbranehed polyestersand polyurethane coatings[J].Journal of Polymer Science Part A:Polymer Chemistry,2007,45(13):2673-2688. |
| [5] | 高喜平,王勃,曹光宇,李俊贤,张玉清.异佛尔酮二异氰酸酯分子中异氰酸酯基团活性比较[J].河南科技大学学报（自然科学版）,2009(02):101-104. |
| [6] | 李晓萱,何国平,伍胜利.水性聚氨酯的硬段结晶与粘接性能[J].高分子材料科学与工程,2009(03):71-74. |
| [7] | 黎庆安,孙东成,王玉香.HDI-IPDI型高固含量水性聚氨酯分散体的合成及微观形态[J].高分子材料科学与工程,2007(03):59-62. |
| [8] | LI YINGJIE;KANG WANXUAN;STOFFER JAMES O et al.Effect of hard-segment flexibility on phase separation of segmented polyurethane[J].Macromolecules,1994,27:612-614. |
| [9] | 刘景芳,李树材.硬段含量对水性聚氨酯性能的影响[J].涂料工业,2004(08):5-10. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%