以有机硅改性的丙烯酸酯乳液为基料,多聚磷酸铵(APP)、季戊四醇(PER)、三聚氰胺(MEL)为膨胀阻燃体系,制备水性超薄膨胀型钢结构防火涂料;采用硼酸和可膨胀石墨(EG)改性防火涂料.研究表明,同时用w(硼酸)=4%,w(EG)=5%改性防火涂料,涂层的耐火极限达到93 min,热失质量分析(TGA)测试表明w(硼酸)=4%,w(EG)=5%共同改性的防火涂料在700℃时最终残炭量是44%.扫描电镜(SEM)分析结果表明硼酸/EG改性的残炭层形成了致密的"蜂窝"状结构.
参考文献
| [1] | BRAS M L;BOURBIGOT S .Comprehensive study of the degradation of all intumescent EVA-based material during combustion[J].Journal of Materials Science,1999,34(23):5777-5782. |
| [2] | 杨卫疆,诸秋萍,陆亨荣,林桂祥.膨胀型防火涂料炭化层形成过程的探讨[J].化学建材,2001(06):20-23. |
| [3] | Jun-wei Gu;Guang-cheng Zhang;Shan-lai Dong;Qiu-yu Zhang;Jie Kong .Study on preparation and fire-retardant mechanism analysis of intumescent flame-retardant coatings[J].Surface & Coatings Technology,2007(18):7835-7841. |
| [4] | 李飞,余历军,张星雨,陆江丽.超薄膨胀型钢结构防火涂料的研制[J].涂料工业,2007(03):42-44. |
| [5] | 关迎东,李少香.膨胀型饰面防火涂料现状及进展[J].中国涂料,2009(03):19-23,28. |
| [6] | Jimenez M;Duquesne S;Bourbigot S .Intumescent fire protective coating: Toward a better understanding of their mechanism of action[J].Thermochimica Acta: An International Journal Concerned with the Broader Aspects of Thermochemistry and Its Applications to Chemical Problems,2006(1/2):16-26. |
| [7] | 刘学军,付若愚,咸才军,郭保文,郭奋.可膨胀石墨在膨胀型钢结构防火涂料中的应用[J].精细化工,2005(05):328-330,341. |
| [8] | 李国新,梁国正,杨秦莉,宋学锋.可膨胀石墨改性APP/PER/MEL防火涂料的热降解研究[J].涂料工业,2006(11):11-14,18. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%